X 5 CrNiMo 17 12 2

DIN EN 10088-3:1995 — Stainless steels - Part 3:Technical delivery conditions for semi-finished products,bars,rods,wires,sections and bright products of corrosion resisting steels for general purposes

Chemical composition

ElementminmaxSimilarRemarks
C0.07
Cr16.518.5
Mn2
Mo22.5
N0.11
Ni1013
P0.045
S0.03
Si1

Mechanical properties

Heat treatment / conditionYield strengthTensile strengthElongationReduction of areaImpact energyHardness
Wires +C1100, >= 0.05 mm1100–1350
Wires +C600, >= 0.05 mm600–800
Wires +C700, >= 0.05 mm700–900
Wires +C800, >= 0.05 mm800–1000
Wires +C900, >= 0.05 mm900–1100
Wires +C1000, >= 0.05 mm1000–1250
Wires +C1200, >= 0.05 mm1200–1450
Wires +C1400, >= 0.05 mm1400–1700
Wires +C1600, >= 0.05 mm1600–1900
Wires +C1800, >= 0.05 mm1800–2100
Wires +C500, >= 0.05 mm500–700
Wires +AT, > 0.05 <= 0.1 mm≤1100≥20
Wires +AT, > 0.1 <= 0.2 mm≤1050≥20
Wires +AT, > 0.2 <= 0.5 mm≤1000≥30
Wires +AT, > 0.5 <= 1 mm≤950≥30
Wires +AT, > 1 <= 3 mm≤900≥30
Wires +AT, > 3 <= 5 mm≤850≥35
Wires +AT, > 5 <= 16 mm≤800≥35
rods, bars, wire, sections, bright products +AT, <= 160 mm≥200500–700≥30 After fracture; (trans.)≥100 KV (ISO-V) (trans.)HB ≤215
rods, bars, wire, sections, bright products +AT, > 160 <= 250 mm≥200500–700≥30 After fracture; (long.)≥60 KV (ISO-V) (trans.)HB ≤215
bars +C700, < 35 mm≥350700–850≥20 after fracture
bars +C800, < 25 mm≥500800–1000≥12 after fracture
bars +AT, <= 10 mm≥400600–950≥25 (纵向)
bars +AT, > 10 <= 16 mm≥380580–950≥25 (纵向)
bars +AT, > 16 <= 63 mm≥200500–850≥30 (纵向)≥100 (纵向)
bars +AT, > 160 <= 250 mm≥200500–700≥30 (横向)≥60 (横向)
bars +AT, > 63 <= 160 mm≥200500–700≥40 (纵向)≥100 (纵向)

Physical properties

20.0

Elastic modulusMean thermal expansionThermal conductivitySpecific heatResistivityDensityPoisson's ratio
200.00；180.00；190.00；175.0015.00；14.10500.000.758.00；7.96；8.030.31

Typical physical values

DensityElastic modulusPoisson's ratioRemarks
7.61–8.10190.00–215.000.27–0.30不锈钢的典型材料性能数值，此值不来源于标准，它是指示性指标，不能被用于设计用途。
7.86190.00–210.000.27–0.30低碳，高合金钢材料性能属性数值，此值不来源于标准，它是指示性指标，不能被用于设计用途。

High/low temperature

Yield strength Rp0.2 (MPa)
ConditionTemperature ℃Approx.
solution annealed +AT550108
solution annealed +AT500110
solution annealed +AT450112
solution annealed +AT400115
solution annealed +AT350120
solution annealed +AT300127
solution annealed +AT250135
solution annealed +AT200145
solution annealed +AT150158
solution annealed +AT100175

Creep

Temperature ℃Time hCRS
60010000.0h176.0
600100000.0h118.0
65010000.0h111.0
650100000.0h69.0
70010000.0h65.0
700100000.0h34.0
75010000.0h42.0
750100000.0h20.0
80010000.0h24.0
800100000.0h10.0

Similar grades

GradeRegionSystem
4436-316-00-IInternational standardISO
4401-316-00-IInternational standardISO
A313 S31600United StatesASTM
06Cr17Ni12Mo2ChinaGB
A240 S31600United StatesASTM
S31608ChinaGB
1.4401ItalyUNI
X 5 CrNiMo 17 12 2ItalyUNI
1.4401SpainUNE
X 5 CrNiMo 17 12 2SpainUNE
1.4401RomaniaSTAS
X 5 CrNiMo 17 12 2RomaniaSTAS
1.4401SwedenSS
X 5 CrNiMo 17 12 2SwedenSS
1.4401SwitzerlandSNV
X 5 CrNiMo 17 12 2SwitzerlandSNV
1.4401FinlandSFS
X 5 CrNiMo 17 12 2FinlandSFS
1.4401PolandPN
X 5 CrNiMo 17 12 2PolandPN
1.4401AustriaONORM
X 5 CrNiMo 17 12 2AustriaONORM
1.4401NorwayNS
X 5 CrNiMo 17 12 2NorwayNS
1.4401BelgiumNBN
X 5 CrNiMo 17 12 2BelgiumNBN
1.4401HungaryMSZ
X 5 CrNiMo 17 12 2HungaryMSZ
1.4401Czech RepublicCSN
X 5 CrNiMo 17 12 2Czech RepublicCSN
1.4401BulgariaBDS
X 5 CrNiMo 17 12 2BulgariaBDS
1.4401United KingdomB.S.
X 5 CrNiMo 17 12 2United KingdomB.S.
1.4401FranceAFNOR NF
PK332GlobalEnterprise standard
Remanit 4435 SUPER IMGlobalEnterprise standard
Remanit 4435GlobalEnterprise standard
Remanit 4429GlobalEnterprise standard
Remanit 4404 SUPER IMGlobalEnterprise standard
Remanit 4404 IMGlobalEnterprise standard
Remanit 4404GlobalEnterprise standard
Remanit 4401 SUPER IMGlobalEnterprise standard
Remanit 4401 IMGlobalEnterprise standard
Remanit 4401GlobalEnterprise standard
IMCO316LMGlobalEnterprise standard
IMCO316LGlobalEnterprise standard
IMCO316GlobalEnterprise standard
316LMGlobalEnterprise standard
316LM/1GlobalEnterprise standard
CLC 17-13-3LNGlobalEnterprise standard
CLC 17-12-2LGlobalEnterprise standard
Type 316GlobalEnterprise standard
SANMAC 4435GlobalEnterprise standard
SANMAC 316LGlobalEnterprise standard
SANMAC 316GlobalEnterprise standard
Bioline 316LVMGlobalEnterprise standard
3R60GlobalEnterprise standard
3R60 Urea GradeGlobalEnterprise standard
BÖHLER A200GlobalEnterprise standard
Project 70+ Type 316/316L StainlessGlobalEnterprise standard
Carpenter Stainless Type 316LNGlobalEnterprise standard
Carpenter Stainless Type 316/316LGlobalEnterprise standard
X3CrNiMo17-12-3International standardISO
X5CrNiMo17-12-2International standardISO
A182 F 316United StatesASTM
A240 Type 316LUnited StatesASTM
AISI 316LUnited StatesAISI
AISI 316United StatesAISI
316United StatesSAE
08H17N13M2TRussiaGOST
SUS 316LJapanJIS
SUS 316JapanJIS
X 5 CrNiMo 17 12 2FranceAFNOR NF
1.4429European UnionEN
1.4436European UnionEN
1.4435European UnionEN
1.4432European UnionEN
X 3 CrNiMo 17 13 3European UnionEN
X 2 CrNiMo 18 14 3European UnionEN
X 2 CrNiMo 17 12 2European UnionEN
X 5 CrNiMo 17 13 3GermanyDIN
X 2 CrNiMo 17 13 2GermanyDIN
X 5 CrNiMo 18 10GermanyDIN
X 3 CrNiMo 17 13 3GermanyDIN
X 2 CrNiMo 18 14 3GermanyDIN
X 2 CrNiMo 17 12 3GermanyDIN
X 2 CrNiMoN 17 13 3GermanyDIN
X 2 CrNiMo 17 12 2GermanyDIN
1.4435GermanyDIN
1.4429GermanyDIN
1.4404GermanyDIN
1.4401GermanyDIN
1Cr17Ni12Mo2ChinaGB
0Cr18Ni12Mo2TiChinaGB
0Cr17Ni12Mo2ChinaGB