Fatigue Condition 1. 1.Flat products; Thickness (mm): 1; Cold worked 37%; Reversed bending; T: 20°C; - 2. 2.Flat products; Thickness (mm): 1; 冷加工60%; Reversed bending; T: 20°C; - 3. 3.钢棒; Diameter (mm): 7.6; 退火; Rotating beam; T: 20°C; Rod 4. 4.钢棒; Diameter (mm): 7.6; Cold worked 36%; Rotating beam; T: 20°C; Rod 5. 5.钢棒; Diameter (mm): 16; 冷加工30%; Rotating beam; T: 20°C; Rod 6. 6.钢棒; Diameter (mm): 25.4; Cold worked 35%; Rotating beam; T: 20°C; Rod 7. 7.钢带; Thickness (mm): 0.8; Cold worked 21%; Reversed bending; T: 20°C; - 8. 8.钢带; Thickness (mm): 0.8; Cold worked 37%; Reversed bending; T: 20°C; - 9. 9.钢带; Thickness (mm): 0.8; 冷加工60%; Reversed bending; T: 20°C; - 10. 10.钢带; Thickness (mm): 0.5; 退火; Reversed bending; T: 20°C; - 11. 11.钢带; Thickness (mm): 0.5; 冷加工60%; Reversed bending; T: 20°C; - 12. 12.钢带; Thickness (mm): 0.5; 冷加工 20%; Reversed bending; T: 20°C; - 13. 13.Flat products; Thickness (mm): 1; 退火; Reversed bending; T: 20°C; - 14. 14.Flat products; Thickness (mm): 1; Cold worked 21%; Reversed bending; T: 20°C; - 1.Flat products; Thickness (mm): 1; Cold worked 37%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product Flat products; Thickness (mm): 1; Cold worked 37% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 345.0
Stress life 2.Flat products; Thickness (mm): 1; 冷加工60%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product Flat products; Thickness (mm): 1; cold worked 60% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 379.0
Stress life 3.钢棒; Diameter (mm): 7.6; 退火; Rotating beam; T: 20°C; Rod
Test conditions Item Detail Product steel bar; Diameter (mm): 7.6; annealed Experiment Rotating beam; T: 20°C Specimen Rod
Monotonic Property Value Tensile strength (MPa) 214.0
Stress life 4.钢棒; Diameter (mm): 7.6; Cold worked 36%; Rotating beam; T: 20°C; Rod
Test conditions Item Detail Product steel bar; Diameter (mm): 7.6; Cold worked 36% Experiment Rotating beam; T: 20°C Specimen Rod
Monotonic Property Value Tensile strength (MPa) 336.0
Stress life 5.钢棒; Diameter (mm): 16; 冷加工30%; Rotating beam; T: 20°C; Rod
Test conditions Item Detail Product steel bar; Diameter (mm): 16; cold worked 30% Experiment Rotating beam; T: 20°C Specimen Rod
Monotonic Property Value Tensile strength (MPa) 303.0
Stress life 6.钢棒; Diameter (mm): 25.4; Cold worked 35%; Rotating beam; T: 20°C; Rod
Test conditions Item Detail Product steel bar; Diameter (mm): 25.4; Cold worked 35% Experiment Rotating beam; T: 20°C Specimen Rod
Monotonic Property Value Tensile strength (MPa) 331.0
Stress life 7.钢带; Thickness (mm): 0.8; Cold worked 21%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; Cold worked 21% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 283.0
Stress life 8.钢带; Thickness (mm): 0.8; Cold worked 37%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; Cold worked 37% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 340.0
Stress life 9.钢带; Thickness (mm): 0.8; 冷加工60%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; cold worked 60% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 398.0
Stress life 10.钢带; Thickness (mm): 0.5; 退火; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.5; annealed Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 216.0
Stress life 11.钢带; Thickness (mm): 0.5; 冷加工60%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.5; cold worked 60% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 363.0
Stress life 12.钢带; Thickness (mm): 0.5; 冷加工 20%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.5; cold worked 20% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 306.0
Stress life 13.Flat products; Thickness (mm): 1; 退火; Reversed bending; T: 20°C; -
Test conditions Item Detail Product Flat products; Thickness (mm): 1; annealed Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 234.0
Stress life 14.Flat products; Thickness (mm): 1; Cold worked 21%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product Flat products; Thickness (mm): 1; Cold worked 21% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 290.0
Stress life 
European Union · EN
Italy
Spain
Sweden
Switzerland
Finland
Poland
Austria
Norway
Belgium
Hungary
Germany
United Kingdom
Romania
France
United States