European Union · EN
Cu-FRTP
EN 1652:1997 — EN 1652
Chemical composition
| Element | min | max | Similar | Remarks |
|---|---|---|---|---|
| Cu | 99.9 | Analysis value for Cu may contain Ag. For this grade Ag=max 0.015%; | Analysis value for Cu may contain Ag. For this grade Ag=max 0.015%; | |
| O | 0.1 | |||
| Total Others | 0.05 | Excluding Ag | Excluding Ag |
Mechanical properties
| Heat treatment / condition | Yield strength | Tensile strength | Elongation | Reduction of area | Impact energy | Hardness |
|---|---|---|---|---|---|---|
| Circles, plates, sheets, strips, R200, t > 5 mm | 200.00 | 42.00 | ||||
| Circles, plates, sheets, strips, R220, 0.2 < t <= 5.0 mm | 220.00 | 33.00 | ||||
| Circles, plates, sheets, strips, R240, 0.2 < t <= 15.0 mm | 180.00 | 240.00 | 8.00 | |||
| Circles, plates, sheets, strips, R290, 0.2 < t <= 15.0 mm | 250.00 | 290.00 | 4.00 | |||
| Circles, plates, sheets, strips, R360, 0.2 < t <= 2.0 mm | 320.00 | 360.00 | 2.00 | |||
| Circles, sheets, strips, H040, 0.2 < t <= 5.0 mm, HV | plates 40.00 | |||||
| Circles, sheets, strips, H040, t > 5 mm, HV | plates 40.00 | |||||
| Circles, sheets, strips, H065, 0.2 < t <= 15.0 mm, HV | plates 65.00 | |||||
| Circles, sheets, strips, H090, 0.2 < t <= 15.0 mm, HV | plates 90.00 | |||||
| Circles, sheets, strips, H110, 0.2 < t <= 2.0 mm, HV | plates 110.00 |
Physical properties
| Elastic modulus | Mean thermal expansion | Thermal conductivity | Specific heat | Resistivity | Density | Poisson's ratio |
|---|---|---|---|---|---|---|
| 8.90 |
Fatigue
1.Flat products; Thickness (mm): 1; Cold worked 37%; Reversed bending; T: 20°C; -
| Item | Detail |
|---|---|
| Product | Flat products; Thickness (mm): 1; Cold worked 37% |
| Experiment | Reversed bending; T: 20°C |
| Specimen |
| Property | Value |
|---|---|
| Tensile strength (MPa) | 345.0 |
| No. | Cycles |
|---|---|
| 1 | 1E8 |
Similar grades
| Grade | Region | System |
|---|---|---|
| CR006A |  Italy | UNI |
| CR006A |  Spain | UNE |
| CR006A |  Sweden | SS |
| CR006A |  Switzerland | SNV |
| CR006A |  Finland | SFS |
| CR006A |  Poland | PN |
| CR006A |  Austria | ONORM |
| CR006A |  Norway | NS |
| CR006A |  Belgium | NBN |
| CR006A |  Hungary | MSZ |
| CR006A |  Germany | DIN |
| CR006A | Czech Republic | CSN |
| CR006A |  United Kingdom | B.S. |
| CR006A | Bulgaria | BDS |
| CR006A |  Romania | ASRO |
| CR006A |  France | AFNOR NF |
| CW006A | Italy | UNI |
| CW006A | Spain | UNE |
| Cu-FRTP | Spain | UNE |
| CW006A | Sweden | SS |
| Cu-FRTP | Sweden | SS |
| CW006A | Switzerland | SNV |
| Cu-FRTP | Switzerland | SNV |
| CW006A | Finland | SFS |
| Cu-FRTP | Finland | SFS |
| CW006A | Poland | PN |
| Cu-FRTP | Poland | PN |
| CW006A | Austria | ONORM |
| Cu-FRTP | Austria | ONORM |
| CW006A | Norway | NS |
| Cu-FRTP | Norway | NS |
| CW006A | Belgium | NBN |
| Cu-FRTP | Belgium | NBN |
| CW006A | Hungary | MSZ |
| Cu-FRTP | Hungary | MSZ |
| CW006A | Germany | DIN |
| CW006A | Czech Republic | CSN |
| Cu-FRTP | Czech Republic | CSN |
| CW006A | United Kingdom | B.S. |
| Cu-FRTP | United Kingdom | B.S. |
| CW006A | Bulgaria | BDS |
| Cu-FRTP | Bulgaria | BDS |
| CW006A | Romania | ASRO |
| Cu-FRTP | Romania | ASRO |
| CW006A | France | AFNOR NF |
| Cu-FRTP | France | AFNOR NF |
| CR006A | European Union | EN |
| Cu FRTP | Italy | UNI |
| CW006A | European Union | EN |
| C12200 |  United States | UNS |
| 2.0090 | Germany | DIN |
| 2.0076 | Germany | DIN |
| Cu-FRTP | Germany | DIN |
| SF-Cu | Germany | DIN |
| SW-Cu | Germany | DIN |