德国 · DIN
1.0562
DIN EN 10217-3:2005 — 承压焊接钢管 - 交货技术条件 - 第3部分：细粒合金钢管
化学成分
| 元素 | min | max | 相似 | 备注 |
|---|---|---|---|---|
| Al | 0.02 | Al/N=>2 | Al/N=>2 | |
| C | 0.2 | |||
| Cr | 0.3 | |||
| Cr+Cu+Mo | The sum of the percentage by mass of the three elements Cr | The sum of the percentage by mass of the three elements Cr | ||
| Cu | 0.3 | |||
| Mn | 0.9 | 1.7 | ||
| Mo | 0.08 | |||
| N | 0.02 | |||
| Nb | 0.05 | |||
| Nb+Ti+V | 0.12 | |||
| Ni | 0.5 | |||
| P | 0.025 | |||
| S | 0.02 | |||
| Si | 0.5 | |||
| Ti | 0.03 | |||
| V | 0.1 |
力学性能
| 热处理 / 状态 | 屈服强度 | 抗拉强度 | 伸长率 | 断面收缩率 | 冲击功 | 硬度 |
|---|---|---|---|---|---|---|
| 焊接钢管 正火(N) 12 < T <= 20 mm | ≥355 or Upper yield stress | 490–650 | ≥22 long. test | |||
| 焊接钢管 正火(N) 20 < T <= 40 mm | ≥345 or Upper yield stress | 490–630 | ≥22 long. test | |||
| 焊接钢管 正火(N) T <= 12 mm (t - 壁厚) | ≥355 or Upper yield stress | 490–650 | ≥22 long. test | |||
| 焊接钢管 焊接处理 | ≥39 KV (20°C)；≥31 KV (-10°C)；≥31 KV (-0°C)；≥27 KV (-20°C)；≥55 KV (20°C)；≥47 KV (0°C)；≥43 KV (-10°C)；≥40 KV (-20°C) |
物理性能
-100.0
| 弹性模量 | 平均热膨胀系数 | 热导率 | 比热容 | 电阻率 | 密度 | 泊松比 |
|---|---|---|---|---|---|---|
| 217.00 | 10.80 | 37.60 | 371.00 | 0.18 |
典型物理值
| 密度 | 弹性模量 | 泊松比 | 备注 |
|---|---|---|---|
| 7.86 | 203.00 | 0.27–0.30 | 低碳，低合金钢的典型性能数值。此值不来源于标准，它是指示性指标，不能被用于设计用途。 |
高/低温力学性能
| 热处理 / 状态 | 温度 ℃ | min | 备注 |
|---|---|---|---|
| 焊接钢管 焊接处理 | -10 | 31 | KV |
| 焊接钢管 焊接处理 | -20 | 27 | KV |
| 焊接钢管 焊接处理 | 0 | 31 | KV |
| 焊接钢管 焊接处理 | -10 | 43 | KV |
| 焊接钢管 焊接处理 | -20 | 40 | KV |