C19400 under --

Chemical composition

Element	min	max
Cu	97
Fe	2.1	2.6
P	0.015	0.15
Pb		0.03
Zn	0.05	0.2

Physical properties

Temperature

-200.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
128.00

-125.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
126.00

-75.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
124.00

20.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
121.00		259.60	385.50	0.03	8.91	0.33

25.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
121.00

100.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
118.00

150.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
116.00

200.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
114.00

300.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	17.60

Fatigue

Condition

1.扁钢; 0.64 mm thick; Soft annealed (O60); Rotating beam; T: 20°C; -

Test conditions

Item	Detail
Product	flat; 0.64 mm thick; Soft annealed (O60)
Experiment	Rotating beam; T: 20°C
Specimen

Monotonic

Property	Value
Elastic modulus (GPa)	121.0
Yield strength (MPa)	150.0
Tensile strength (MPa)	310.0
Elongation (%)	29.0
Hardness (HRB)	38.0

Stress life

No.	Cycles
1	E8

2.扁钢; 1 mm thick; Hard (H04); Rotating beam; T: 20°C; -

Test conditions

Item	Detail
Product	flat; 1 mm thick; Hard (H04)
Experiment	Rotating beam; T: 20°C
Specimen

Monotonic

Property	Value
Elastic modulus (GPa)	121.0
Yield strength (MPa)	380.0
Tensile strength (MPa)	450.0
Elongation (%)	7.0
Hardness (HRB)	73.0

Stress life

No.	Cycles
1	E8

3.扁钢; 1 mm thick; Cold worked - spring (H08); Rotating beam; T: 20°C; -

Test conditions

Item	Detail
Product	flat; 1 mm thick; Cold worked - spring (H08)
Experiment	Rotating beam; T: 20°C
Specimen

Monotonic

Property	Value
Elastic modulus (GPa)	121.0
Yield strength (MPa)	486.0
Tensile strength (MPa)	505.0
Elongation (%)	3.0
Hardness (HRB)	75.0

Stress life

No.	Cycles
1	E8

4.扁钢; 1 mm thick; Cold worked - extra spring (H10); Rotating beam; T: 20°C; -

Test conditions

Item	Detail
Product	flat; 1 mm thick; Cold worked - extra spring (H10)
Experiment	Rotating beam; T: 20°C
Specimen

Monotonic

Property	Value
Elastic modulus (GPa)	121.0
Yield strength (MPa)	507.0
Tensile strength (MPa)	530.0
Elongation (%)	2.0
Hardness (HRB)	77.0

Stress life

No.	Cycles
1	E8

5.钢管; 0.635 mm; 退火; T: 20°C; -

Test conditions

Item	Detail
Product	steel tube; 0.635 mm; annealed
Experiment	T: 20°C
Specimen

Monotonic

Property	Value
Elastic modulus (GPa)	121.0
Yield strength (MPa)	214.0
Tensile strength (MPa)	310.0
Elongation (%)	32.0
Hardness (HRB)	38.0

Stress life

No.	Cycles
1	E8

Similar grades

Grade	Region	System
2.0205	Germany	DIN
2.1310	Germany	DIN
B888 C19400	United States	ASTM
CW107C	Germany	DIN
CW119C	Germany	DIN
SB-543 C19400	United States	ASME
B694 C19400	United States	ASTM
B543 C19400	United States	ASTM
B465 C19400	United States	ASTM
CW107C	European Union	EN
CW119C	European Union	EN
CuFe2P	European Union	EN
CuZn0	5	European Union
CuZn0	5	Germany
CuFe2P	Germany	DIN