Fatigue Condition 1. 1.钢带; Thickness (mm): 1; Solution heat treated and cold worked 37%; Reversed bending; T: 20°C; - 2. 2.钢带; Thickness (mm): 0.8; 沉淀硬化; 3h at 316°C in purified nitrogen; Reversed bending; T: 20°C; - 3. 3.钢带; Thickness (mm): 0.8; 沉淀硬化; 3h at 316°C in muffle furnace; Reversed bending; T: 20°C; - 4. 4.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 21%; 2h at 316°C in purified nitrogen; Reversed bending; T: 20°C; - 5. 5.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 21%; 2h at 316°C in muffle nitrogen; Reversed bending; T: 20°C; - 6. 6.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 37%; 2h at 316°C in purified nitrogen; Reversed bending; T: 20°C; - 7. 7.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 37%; 2h at 316°C in muffle nitrogen; Reversed bending; T: 20°C; - 8. 8.钢带; Thickness (mm): 0.8; 沉淀硬化; 3h at 316°C; Reversed bending; T: 20°C; - 9. 9.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 11%; 2h at 316°C; Reversed bending; T: 20°C; - 10. 10.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 21%; 2h at 316°C; Reversed bending; T: 20°C; - 11. 11.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 37%; 2h at 316°C; Reversed bending; T: 20°C; - 12. 12.钢带; Thickness (mm): 1; 沉淀硬化; Reversed bending; T: 20°C; - 13. 13.钢带; Thickness (mm): 1; 沉淀硬化; After cold working 21%; Reversed bending; T: 20°C; - 14. 14.钢带; Thickness (mm): 1; 沉淀硬化; After cold working 37%; Reversed bending; T: 20°C; - 15. 15.钢棒; Diameter (mm): 13; 沉淀硬化; Alternating torsion; T: 20°C; - 16. 16.钢棒; Diameter (mm): 16; 沉淀硬化; 3h at 316°C; Rotating beam; T: 20°C; - 17. 17.Wires; 沉淀硬化; Bending; T: 20°C; - 18. 18.Wires; 沉淀硬化; After cold drawing; Bending; T: 20°C; - 19. 19.Wires; 沉淀硬化; After cold drawing; Rotating cantilever; T: 20°C; - 20. 20.钢带; Thickness (mm): 0.8; 固溶热处理; Reversed bending; T: 20°C; - 21. 21.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 21%; Rm [MPa]: 600; Reversed bending; T: 20°C; - 22. 22.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 37%; Rm [MPa]: 800; Reversed bending; T: 20°C; - 23. 23.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 11%; Reversed bending; T: 20°C; - 24. 24.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 21%; Rm [MPa]: 690; Reversed bending; T: 20°C; - 25. 25.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 37%; Rm [MPa]: 810; Reversed bending; T: 20°C; - 26. 26.钢带; Thickness (mm): 1; 固溶热处理; Reversed bending; T: 20°C; - 27. 27.钢带; Thickness (mm): 1; Solution heat treated and cold worked 21%; Reversed bending; T: 20°C; - 1.钢带; Thickness (mm): 1; Solution heat treated and cold worked 37%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 1; Solution heat treated and cold worked 37% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 758.0
Stress life 2.钢带; Thickness (mm): 0.8; 沉淀硬化; 3h at 316°C in purified nitrogen; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; 3h at 316°C in purified nitrogen Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1043.0
Stress life 3.钢带; Thickness (mm): 0.8; 沉淀硬化; 3h at 316°C in muffle furnace; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; 3h at 316°C in muffle furnace Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 995.0
Stress life 4.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 21%; 2h at 316°C in purified nitrogen; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; After cold working 21%; 2h at 316°C in purified nitrogen Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1202.0
Stress life 5.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 21%; 2h at 316°C in muffle nitrogen; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; After cold working 21%; 2h at 316°C in muffle nitrogen Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1244.0
Stress life 6.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 37%; 2h at 316°C in purified nitrogen; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; After cold working 37%; 2h at 316°C in purified nitrogen Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1302.0
Stress life 7.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 37%; 2h at 316°C in muffle nitrogen; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; After cold working 37%; 2h at 316°C in muffle nitrogen Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1003.0
Stress life 8.钢带; Thickness (mm): 0.8; 沉淀硬化; 3h at 316°C; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; 3h at 316°C Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1304.0
Stress life 9.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 11%; 2h at 316°C; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; After cold working 11%; 2h at 316°C Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1318.0
Stress life 10.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 21%; 2h at 316°C; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; After cold working 21%; 2h at 316°C Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1405.0
Stress life 11.钢带; Thickness (mm): 0.8; 沉淀硬化; After cold working 37%; 2h at 316°C; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; precipitation hardened; After cold working 37%; 2h at 316°C Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1447.0
Stress life 12.钢带; Thickness (mm): 1; 沉淀硬化; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 1; precipitation hardened Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1209.0
Stress life 13.钢带; Thickness (mm): 1; 沉淀硬化; After cold working 21%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 1; precipitation hardened; After cold working 21% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1344.0
Stress life 14.钢带; Thickness (mm): 1; 沉淀硬化; After cold working 37%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 1; precipitation hardened; After cold working 37% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1379.0
Stress life 15.钢棒; Diameter (mm): 13; 沉淀硬化; Alternating torsion; T: 20°C; -
Test conditions Item Detail Product steel bar; Diameter (mm): 13; precipitation hardened Experiment Alternating torsion; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 793.0
Stress life 16.钢棒; Diameter (mm): 16; 沉淀硬化; 3h at 316°C; Rotating beam; T: 20°C; -
Test conditions Item Detail Product steel bar; Diameter (mm): 16; precipitation hardened; 3h at 316°C Experiment Rotating beam; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1230.0
Stress life 17.Wires; 沉淀硬化; Bending; T: 20°C; -
Test conditions Item Detail Product Wires; precipitation hardened Experiment Bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1227.0
Stress life 18.Wires; 沉淀硬化; After cold drawing; Bending; T: 20°C; -
Test conditions Item Detail Product Wires; precipitation hardened; After cold drawing Experiment Bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1324.0
Stress life No. Cycles 1 1E8 2 1E8 3 1E8 4 1E8
19.Wires; 沉淀硬化; After cold drawing; Rotating cantilever; T: 20°C; -
Test conditions Item Detail Product Wires; precipitation hardened; After cold drawing Experiment Rotating cantilever; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 1324.0
Stress life No. Cycles 1 1E8 2 1E8 3 1E8 4 1E8
20.钢带; Thickness (mm): 0.8; 固溶热处理; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; solution treated Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 498.0
Stress life 21.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 21%; Rm [MPa]: 600; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; Solution heat treated and cold worked 21%; Rm [MPa]: 600 Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 587.0
Stress life 22.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 37%; Rm [MPa]: 800; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; Solution heat treated and cold worked 37%; Rm [MPa]: 800 Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 783.0
Stress life 23.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 11%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; Solution heat treated and cold worked 11% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 573.0
Stress life 24.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 21%; Rm [MPa]: 690; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; Solution heat treated and cold worked 21%; Rm [MPa]: 690 Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 676.0
Stress life 25.钢带; Thickness (mm): 0.8; Solution heat treated and cold worked 37%; Rm [MPa]: 810; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 0.8; Solution heat treated and cold worked 37%; Rm [MPa]: 810 Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 793.0
Stress life 26.钢带; Thickness (mm): 1; 固溶热处理; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 1; solution treated Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 476.0
Stress life 27.钢带; Thickness (mm): 1; Solution heat treated and cold worked 21%; Reversed bending; T: 20°C; -
Test conditions Item Detail Product steel strip; Thickness (mm): 1; Solution heat treated and cold worked 21% Experiment Reversed bending; T: 20°C Specimen
Monotonic Property Value Tensile strength (MPa) 641.0
Stress life 
European Union · EN
Germany
Italy
Spain
Sweden
Switzerland
Finland
Poland
Austria
Norway
Belgium
Hungary
United Kingdom
Romania
France
United States