PSL2 Grade L415QS
UNE EN ISO 3183
Chemical composition
| Element | min | max | Similar | Remarks |
|---|---|---|---|---|
| Al | 0.06 | Al total | Al total | |
| B | 0.0005 | |||
| C | 0.16 | For each reduction of 0.01% below the specified max.concentration for C | For each reduction of 0.01% below the specified max.concentration for C | |
| CE Pcm | 0.22 | Product analysis C＜=0.12% | Product analysis C＜=0.12% | |
| CEV | 0.41 | The CEV limits apply if C＞0.12% | The CEV limits apply if C＞0.12% | |
| Ca | 0.006 | For SMLS and welded pipes;For welded pipe where calcium is intentionally added | For SMLS and welded pipes;For welded pipe where calcium is intentionally added | |
| Cr | 0.3 | If agreed | If agreed | |
| Cu | 0.35 | If agreed | If agreed | |
| Mn | 1.65 | |||
| Mo | 0.15 | If agreed | If agreed | |
| N | 0.012 | Al/N=＞2:1;Not applicable to titannium-killed or titanium-treated steel. | Al/N=＞2:1;Not applicable to titannium-killed or titanium-treated steel. | |
| Nb | 0.05 | |||
| Nb+Ti+V | 0.15 | |||
| Ni | 0.3 | If agreed | If agreed | |
| P | 0.02 | |||
| S | 0.003 | The max.limit for S may be increased ＜=0.008% for SMLS pipe and | The max.limit for S may be increased ＜=0.008% for SMLS pipe and | |
| Si | 0.45 | |||
| Ti | 0.04 | |||
| V | 0.08 |
Mechanical properties
| Heat treatment / condition | Yield strength | Tensile strength | Elongation | Reduction of area | Impact energy | Hardness |
|---|---|---|---|---|---|---|
| seamless or welded steel tube d > 323.90mm, quenched and tempered | 415–565 Rp0.5 | 520–760 Rp0.5/Rm ratio min.0.93 |