International standard · ISO

2014A

ISO 6362-2:2012 — ISO 6362-2

Chemical composition

wt% · log scale
0.010.1110Cr0.1Cu3.9 – 5Fe0.5Mg0.2 – 0.8Mn0.4 – 1.2Ni0.1Others each0.05Si0.5 – 0.9Ti0.15Ti+Zr0.2Total Others0.15Zn0.25
  • min – max range
  • typical value

Mechanical properties

value range by condition
Yield strength Rp0.2135 MPaTensile strength Rm250 MPaElongation A≤10 %Extruded bars, rods, Annealed +O, 10 mm < D or S <= 200 mmYield strength Rp0.2≤350 MPaTensile strength Rm≤430 MPaElongation A≤6 %Extruded bars, rods, Solution heat treated and artificially aged +T6510, 100 mm < D or S <= 120 mmYield strength Rp0.2≤400 MPaTensile strength Rm≤440 MPaElongation A≤6 %Extruded bars, rods, Solution heat treated and artificially aged +T6510, 12.5 mm < D or S <= 100 mmYield strength Rp0.2≤350 MPaTensile strength Rm≤430 MPaElongation A≤6 %Extruded bars, rods, Solution heat treated and artificially aged +T6510, 120 mm < D or S <= 200 mm

Chemical composition

ElementminmaxSimilarRemarks
Al​​Bal​​​​Bal​​
Cr0.1
Cu3.95
Fe0.5
Mg0.20.8
Mn0.41.2
Ni0.1
Others each0.05
Si0.50.9
Ti0.15
Ti+Zr0.2
Total Others0.15
Zn0.25

Mechanical properties

Heat treatment / conditionYield strengthTensile strengthElongationReduction of areaImpact energyHardness
Extruded bars, rods, Annealed +O, 10 mm < D or S <= 200 mm135250≤10
Extruded bars, rods, Solution heat treated and artificially aged +T6510, 100 mm < D or S <= 120 mm≤350≤430≤6
Extruded bars, rods, Solution heat treated and artificially aged +T6510, 12.5 mm < D or S <= 100 mm≤400≤440≤6
Extruded bars, rods, Solution heat treated and artificially aged +T6510, 120 mm < D or S <= 200 mm≤350≤430≤6
Extruded bars, rods, Solution heat treated and artificially aged +T6511, 100 mm < D or S <= 120 mm≤350≤430≤6
Extruded bars, rods, Solution heat treated and artificially aged +T6511, 12.5 mm < D or S <= 100 mm≤400≤440≤6
Extruded bars, rods, Solution heat treated and artificially aged +T6511, 120 mm < D or S <= 200 mm≤350≤430≤6
Extruded bars, rods, Solution heat treated and naturally aged , 10 mm < D or S <= 200 mm≤240≤345≤10
Extruded bars, rods, Solution heat treated and naturally aged +T4510, 10 mm < D or S <= 200 mm≤240≤345≤10
Extruded bars, rods, Solution heat treated and naturally aged +T4511, 10 mm < D or S <= 200 mm≤240≤345≤10
Extruded bars, rods, solution heat treated artificially aged, 100 mm < D or S <= 120 mm≤350≤430≤6
Extruded bars, rods, solution heat treated artificially aged, 12.5 mm < D or S <= 100 mm≤400≤440≤6
Extruded bars, rods, solution heat treated artificially aged, 120 mm < D or S <= 200 mm≤350≤430≤6
Extruded tubes, Annealed +O, t <= 20 mm≤135≤250≥12 Lo = 5.65√So; A <= 10% in Lo = 50mm
Extruded tubes, Solution heat treated and artificially aged +T6510, 10 < t <= 40 mm≥400≥450≥6 Lo = 5.65√So; A <= 4% in Lo = 50mm
Extruded tubes, Solution heat treated and artificially aged +T6510, t <= 10 mm≥370≥415≥7 Lo = 5.65√So; A <= 8% in Lo = 50mm
Extruded tubes, Solution heat treated and naturally aged , t <= 20 mm≥230≥370≥11 Lo = 5.65√So; A <= 10% in Lo = 50mm
Extruded tubes, Solution heat treated and naturally aged +T4510, t <= 20 mm≥230≥370≥11 Lo = 5.65√So; A <= 10% in Lo = 50mm
Extruded tubes, Solution heat treated and naturally aged +T4511, t <= 20 mm≥230≥370≥11 Lo = 5.65√So; A <= 10% in Lo = 50mm
Extruded tubes, Solution heat treated, quenched, 1 to 3% controlled streched, straightened after stretching and artifically aged +T6510, 10 < t <= 40 mm400.00450.006.00
Extruded tubes, Solution heat treated, quenched, 1 to 3% controlled streched, straightened after stretching and artifically aged +T6510, t <= 10 mm370.00415.007.00
Extruded tubes, Strain-hardened only +H111, t <= 20 mm≤135≤250≥12 Lo = 5.65√So; A <= 10% in Lo = 50mm
Extruded tubes, solution heat treated artificially aged, 10 < t <= 40 mm≥400≥450≥6 Lo = 5.65√So; A <= 4% in Lo = 50mm
Extruded tubes, solution heat treated artificially aged, t <= 10 mm≥370≥415≥7 Lo = 5.65√So; A <= 8% in Lo = 50mm
extruded profiles, Annealed +O, all sizes≤135≤250≥12 Lo = 5.65√So; A <= 10% in Lo = 50mm
extruded profiles, Solution heat treated and artificially aged +T6510, 25 < t <= 75 mm≥415≥460≥7 Lo = 5.65√So
extruded profiles, Solution heat treated and artificially aged +T6510, t <= 25 mm≥370≥415≥7 Lo = 5.65√So; A <= 8% in Lo = 50mm
extruded profiles, Solution heat treated and artificially aged +T6511, 25 < t <= 75 mm≥415≥460≥7 Lo = 5.65√So
extruded profiles, Solution heat treated and artificially aged +T6511, t <= 25 mm≥370≥415≥7 Lo = 5.65√So; A <= 8% in Lo = 50mm
extruded profiles, Solution heat treated and naturally aged , 25 < t <= 75 mm≥270≥410≥10 Lo = 5.65√So
extruded profiles, Solution heat treated and naturally aged , t <= 25 mm≥230≥370≥11 Lo = 5.65√So; A <= 10% in Lo = 50mm
extruded profiles, Solution heat treated and naturally aged +T4510, 25 < t <= 75 mm≥270≥410≥10 Lo = 5.65√So
extruded profiles, Solution heat treated and naturally aged +T4510, t <= 25 mm≥230≥370≥11 Lo = 5.65√So; A <= 10% in Lo = 50mm
extruded profiles, Solution heat treated and naturally aged +T4511, 25 < t <= 75 mm≥270≥410≥10 Lo = 5.65√So
extruded profiles, Solution heat treated and naturally aged +T4511, t <= 25 mm≥230≥370≥11 Lo = 5.65√So; A <= 10% in Lo = 50mm
extruded profiles, Strain-hardened only +H111, all sizes≤135≤250≥12 Lo = 5.65√So; A <= 10% in Lo = 50mm
extruded profiles, solution heat treated artificially aged, 25 < t <= 75 mm≥415≥460≥7 Lo = 5.65√So
extruded profiles, solution heat treated artificially aged, t <= 25 mm≥370≥415≥7 Lo = 5.65√So; A <= 8% in Lo = 50mm