SAE AMS 4410:2007 — SAE AMS 4410

Chemical composition

wt% · log scale
0.010.1110100Cr0.04Cu1.2 – 1.8Fe0.15Mg1.8 – 2.2Mn0.25Others Total0.15Others each0.05Si0.12Ti0.06Zn6.9 – 7.5Zr0.06 – 0.15
  • min – max range
  • typical value

Mechanical properties

value range by condition
Yield strength Rp0.2≥462 MPaTensile strength Rm≥503 MPaElongation A≥9 %Yield strength Rp0.2≥428 MPaTensile strength Rm≥483 MPaElongation A≥4 %Yield strength Rp0.2≥462 MPaTensile strength Rm≥497 MPaElongation A≥10 %Plates, Solution heat treated and artificially overaged +T7451, t: > 101.6 <= 127 mmYield strength Rp0.2≥455 MPaTensile strength Rm≥503 MPaElongation A≥8 %Yield strength Rp0.2≥421 MPaTensile strength Rm≥483 MPaElongation A≥4 %Yield strength Rp0.2≥462 MPaTensile strength Rm≥497 MPaElongation A≥9 %Plates, Solution heat treated and artificially overaged +T7451, t: > 127 <= 152.4 mmYield strength Rp0.2≥448 MPaTensile strength Rm≥503 MPaElongation A≥8 %Yield strength Rp0.2≥421 MPaTensile strength Rm≥476 MPaElongation A≥3 %Yield strength Rp0.2≥455 MPaTensile strength Rm≥497 MPaElongation A≥8 %Plates, Solution heat treated and artificially overaged +T7451, t: > 152.4 <= 177.8 mmYield strength Rp0.2≥462 MPaTensile strength Rm≥510 MPaElongation A≥10 %Yield strength Rp0.2≥462 MPaTensile strength Rm≥510 MPaElongation A≥11 %Plates, Solution heat treated and artificially overaged +T7451, t: > 25.40 <= 50.80 mm

Chemical composition

ElementminmaxSimilarRemarks
Al​​Bal​​​​Bal​​
Cr0.04
Cu1.21.8
Fe0.15
Mg1.82.2
Mn0.25
Others Total0.15
Others each0.05
Si0.12
Ti0.06
Zn6.97.5
Zr0.060.15

Mechanical properties

Heat treatment / conditionYield strengthTensile strengthElongationReduction of areaImpact energyHardness
Plates, Solution heat treated and artificially overaged +T7451, t: > 101.6 <= 127 mm≥462；≥428≥503；≥483；≥497≥9 Lo=50 mm；≥4 Lo=50 mm；≥10 Lo=50 mm
Plates, Solution heat treated and artificially overaged +T7451, t: > 127 <= 152.4 mm≥455；≥421；≥462≥503；≥483；≥497≥8 Lo=50 mm；≥4 Lo=50 mm；≥9 Lo=50 mm
Plates, Solution heat treated and artificially overaged +T7451, t: > 152.4 <= 177.8 mm≥448；≥421；≥455≥503；≥476；≥497≥8 Lo=50 mm；≥3 Lo=50 mm
Plates, Solution heat treated and artificially overaged +T7451, t: > 25.40 <= 50.80 mm≥462≥510≥10 Lo=50 mm；≥11 Lo=50 mm
Plates, Solution heat treated and artificially overaged +T7451, t: > 50.80 <= 76.20 mm≥462；≥434≥510；≥497≥9 Lo=50 mm；≥4 Lo=50 mm；≥10 Lo=50 mm
Plates, Solution heat treated and artificially overaged +T7451, t: > 76.20 <= 101.6 mm≥462；≥428≥503；≥490；≥497≥9 Lo=50 mm；≥4 Lo=50 mm；≥10 Lo=50 mm