International standard · ISO

6360

ISO 6362-2:2012 — ISO 6362-2

Mechanical properties

value range by condition
Yield strength Rp0.2≤110 MPaTensile strength Rm≤150 MPaElongation A≤8 %Extruded bars, rods, Cooled from an elevated temperature shaping process and artificially aged , D or S <= 150 mmYield strength Rp0.2≤150 MPaTensile strength Rm≤195 MPaElongation A≤8 %Extruded bars, rods, Solution heat treated and artificially aged +T66, D or S <= 150 mmYield strength Rp0.2≤50 MPaTensile strength Rm≤110 MPaElongation A≤16 %Extruded bars, rods, Solution heat treated and naturally aged , D or S <= 150 mmYield strength Rp0.2≤140 MPaTensile strength Rm≤185 MPaElongation A≤8 %Extruded bars, rods, solution heat treated artificially aged, D or S <= 150 mm

Mechanical properties

Heat treatment / conditionYield strengthTensile strengthElongationReduction of areaImpact energyHardness
Extruded bars, rods, Cooled from an elevated temperature shaping process and artificially aged , D or S <= 150 mm≤110≤150≤8
Extruded bars, rods, Solution heat treated and artificially aged +T66, D or S <= 150 mm≤150≤195≤8
Extruded bars, rods, Solution heat treated and naturally aged , D or S <= 150 mm≤50≤110≤16
Extruded bars, rods, solution heat treated artificially aged, D or S <= 150 mm≤140≤185≤8
Extruded tubes, Cooled from an elevated temperature shaping process and artificially aged , t <= 15 mm≥120≥150≥8 Lo = 5.65√So; A <= 6% in Lo = 50mm
Extruded tubes, Solution heat treated and artificially aged +T66, t <= 15 mm≥150≥195≥8 Lo = 5.65√So; A <= 6% in Lo = 50mm
Extruded tubes, Solution heat treated and naturally aged , t <= 15 mm≥50≥110≥16 Lo = 5.65√So; A <= 14% in Lo = 50mm
Extruded tubes, solution heat treated artificially aged, t <= 15 mm≥140≥185≥8 Lo = 5.65√So; A <= 6% in Lo = 50mm
extruded profiles, Cooled from an elevated temperature shaping process and artificially aged , t <= 25 mm≥110≥150≥8 Lo = 5.65√So; A <= 6% in Lo = 50mm
extruded profiles, Solution heat treated and artificially aged +T66, t <= 25 mm≥150≥195≥8 Lo = 5.65√So; A <= 6% in Lo = 50mm
extruded profiles, Solution heat treated and naturally aged , t <= 25 mm≥50≥110≥16 Lo = 5.65√So; A <= 14% in Lo = 50mm
extruded profiles, solution heat treated artificially aged, t <= 25 mm≥140≥185≥8 Lo = 5.65√So; A <= 6% in Lo = 50mm