Germany · DIN
1.0425
DIN 17155
Chemical composition
wt% · log scale- min – max range
- typical value
Mechanical properties
value range by conditionCreep properties
- 10000.0h
- 100000.0h
Temperature °C · time at rupture
Fatigue S-N curve
stress vs. cycles (log)- 1.薄板; 20 mm thick; Total strain control; R=-1; T: 23°C; Cylindrical; Diameter [mm]: 10; Gauge length [mm]: 25; 方向: T
- 2.薄板; Total strain control; R=-1; T: 23°C; Cylindrical; Diameter [mm]: 16; Gauge length [mm]: 20; 方向: T
- 3.薄板; Total strain control; R=-1; T: 350°C; Cylindrical; Diameter [mm]: 16; Gauge length [mm]: 40; 方向: T
Chemical composition
| Element | min | max | Similar | Remarks |
|---|---|---|---|---|
| C | 0.2 | |||
| Cr | 0.3 | |||
| Mn | 0.5 | |||
| P | 0.05 | |||
| S | 0.05 | |||
| Si | 0.35 |
Mechanical properties
| Heat treatment / condition | Yield strength | Tensile strength | Elongation | Reduction of area | Impact energy | Hardness |
|---|---|---|---|---|---|---|
| heavy plate, steel strip, normalized, <= 16 mm | ≤260 | ≤410 | ||||
| heavy plate, steel strip, normalized, > 16 <= 40 mm | ≤250 | ≤410 | ||||
| heavy plate, steel strip, normalized, > 40 <= 60 mm | ≤240 | ≤410 |
Fatigue
1.薄板; 20 mm thick; Total strain control; R=-1; T: 23°C; Cylindrical; Diameter [mm]: 10; Gauge length [mm]: 25; 方向: T
| Item | Detail |
|---|---|
| Product | sheet; 20 mm thick |
| Experiment | Total strain control; R=-1; T: 23°C |
| Specimen | Cylindrical; Diameter [mm]: 10; Gauge length [mm]: 25; Direction: T |
| Property | Value |
|---|---|
| Elastic modulus (GPa) | 212.3 |
| Yield strength (MPa) | 316.0 |
| Tensile strength (MPa) | 476.0 |
| Elongation (%) | 22.0 |
| Reduction of area (%) | 66.0 |
| Hardness (HV) | 139.0 |
| Metric | Ferrite pearlite |
| No. | Cyclic yield strength (MPa) | Cyclic strain-hardening exponent n′ | Cyclic strength coefficient K′ (MPa) | Fatigue strength coefficient σ′f (MPa) | Fatigue strength exponent b | Fatigue ductility coefficient ε′f | Fatigue ductility exponent c |
|---|---|---|---|---|---|---|---|
| 1 | 289 | 0.1740 | 853 | 805 | -0.1075 | 0.5529 | -0.5818 |
| No. | Specimen | Stress (MPa) | Cycles |
|---|---|---|---|
| 1 | Cylindrical; Diameter [mm]: 10; Gauge length [mm]: 25; Direction: T | 169 | 2E6 |
Creep
| Temperature ℃ | Time h | Rp1 | CRS |
|---|---|---|---|
| 380 | 10000.0h | 147.1 | 188.29 |
| 380 | 100000.0h | 115.72 | 160.83 |
| 390 | 10000.0h | 133.37 | 172.6 |
| 390 | 100000.0h | 101.01 | 140.24 |
| 400 | 10000.0h | 120.62 | 156.91 |
| 400 | 100000.0h | 88.26 | 122.58 |
| 410 | 10000.0h | 108.85 | 142.2 |
| 410 | 100000.0h | 76.49 | 105.91 |
| 420 | 10000.0h | 98.07 | 127.49 |
| 420 | 100000.0h | 65.7 | 92.18 |
| 430 | 10000.0h | 86.3 | 113.76 |
| 430 | 100000.0h | 56.88 | 81.4 |
| 440 | 10000.0h | 77.47 | 101.01 |
| 440 | 100000.0h | 50.01 | 71.59 |
| 450 | 10000.0h | 68.65 | 90.22 |
| 450 | 100000.0h | 44.13 | 63.74 |
| 460 | 10000.0h | 59.82 | 80.41 |
| 460 | 100000.0h | 38.25 | 55.9 |
| 470 | 10000.0h | 51.98 | 71.59 |
| 470 | 100000.0h | 32.36 | 49.03 |
| 480 | 10000.0h | 44.13 | 63.74 |
| 480 | 100000.0h | 27.46 | 43.15 |
| 490 | 10000.0h | 39.23 | 56.88 |
| 490 | 100000.0h | 23.54 | 37.27 |
| 500 | 10000.0h | 34.32 | 50.99 |
| 500 | 100000.0h | 20.59 | 32.36 |
| 510 | 10000.0h | 30.4 | 47.07 |
| 510 | 100000.0h | 18.63 | 28.44 |
| 520 | 10000.0h | 26.48 | 43.15 |
| 520 | 100000.0h | 16.67 | 25.5 |