2219

-- — -

Chemical composition

wt% · log scale

min – max range
typical value

Mechanical properties

value range by condition

Physical properties

vs. temperature

Elastic modulus GPa

Mean thermal expansion 10⁻⁶/K

Thermal conductivity W/(m·K)

Specific heat J/(kg·K)

Resistivity Ω·mm²/m

Density kg/dm³

Poisson's ratio

Creep properties

0.1h
1.0h
10.0h
100.0h
1000.0h

Temperature °C · time at rupture

Chemical composition

Element	min	max	Remarks
Al			Bal
Cu	5.8	6.8
Fe		0.3
Mg		0.02
Mn	0.2	0.4
Others total		0.05
Si		0.2
Ti	0.02	0.1
Total Others		0.15
V	0.05	0.15
Zn		0.1
Zr	0.1	0.25

Mechanical properties

Heat treatment / condition	Yield strength	Tensile strength	Elongation
Extruded tubes, 12.5 < wt - ≤ 80.00mm, a - ≤ 16.00mm^2, solution heat treated, quenched, or	185	310	12
Extruded tubes, wt - ≤ 12.50mm, a - ≤ 16.00mm^2, solution heat treated, quenched, or	180	290	14
Extruded tubes, wt - ≤ 25.00mm, a - ≤ 16.00mm^2 +T62	≥250	≥370	≥6 Lo=50mm;Amin=5% in Lo=5D or 5.65√A
Extruded tubes, wt - ≤ 25.00mm, a - ≤ 20.00mm^2 +T62	≥250	≥370	≥5 Lo=5D or 5.65√A
Extruded tubes, wt - ≤ 80.00mm, a - ≤ 16.00mm^2, Solution heat treated, cold worked and artificially aged	290.00	400.00	6.00
Extruded tubes, Annealed +O	≤125	≤220	≥12 Lo=50mm;Amin=10% in Lo=5D or 5.65√A

Physical properties

Temperature

-250.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
		15.71

-200.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	17.05	49.90	317.72

-100.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	20.24	93.26	676.79

0.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	21.84	116.92	846.45

20.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
73.08；72.00；70.00	22.05	120.38	865.96	0.04；0.06；0.05	2.84	0.33

25.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
		171.63；171.54；121.15；125.52；112.50；112.97

100.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	22.32；22.77	132.07	915.91

200.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	23.63	143.84	948.43

300.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	24.69	151.35	981.36

400.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	25.86		1026.09

500.0

Elastic modulus	Mean thermal expansion	Thermal conductivity	Specific heat	Resistivity	Density	Poisson's ratio
	26.71		1068.08

Typical physical values

Density	Elastic modulus	Poisson's ratio	Remarks
2.60–2.90	69.00–79.00	0.33	典型性能值: 铝合金。该数值并非来自发行标准，它仅是指标性的，不能用于设计用途。

Fatigue

Condition

1.挤压件、板材; Solution heat treated and artificially aged (T62); Rotating beam; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	extrusion、plate; Solution heat treated and artificially aged (T62)
Experiment	Rotating beam; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Notched	R.R. Moore rotating beam
3	R.R. Moore rotating beam		5E5
4	Notched	R.R. Moore rotating beam

2.挤压件、板材; Solution heat treated and artificially aged (T62); Rotating beam; R=-1; T: 20°C; Notched, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	extrusion、plate; Solution heat treated and artificially aged (T62)
Experiment	Rotating beam; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Notched	R.R. Moore rotating beam
3	R.R. Moore rotating beam		5E5
4	Notched	R.R. Moore rotating beam

3.Plates; Solution heat treated, cold worked approximately 7 % and naturally aged (T37); Completely reversed bending; R=-1; T: 25°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and naturally aged (T37)
Experiment	Completely reversed bending; R=-1; T: 25°C
Specimen	Smooth R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	325.0
Tensile strength (MPa)	385.0
Elongation (%)	12.0

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

4.Plates; Solution heat treated, cold worked approximately 7 % and naturally aged (T37); Completely reversed bending; R=-1; T: 25°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and naturally aged (T37)
Experiment	Completely reversed bending; R=-1; T: 25°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	325.0
Tensile strength (MPa)	385.0
Elongation (%)	12.0

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

5.Plates; 沉淀热处理 (T8511); Completely reversed bending; R=-1; T: 25°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; +T8511
Experiment	Completely reversed bending; R=-1; T: 25°C
Specimen	Smooth R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	340.0
Tensile strength (MPa)	450.0

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam

6.Plates; Thickness >90 mm; Solution heat treated, cold worked and artificially aged (T852); Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Thickness >90 mm; Solution heat treated cold worked and artificially aged (T852)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

7.Plates; Thickness >90 mm; Solution heat treated, cold worked and artificially aged (T852); Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; Thickness >90 mm; Solution heat treated cold worked and artificially aged (T852)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

8.薄板; 1.6 mm; 固溶和沉淀热处理 (T62); Bending; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	sheet; 1.6 mm; +T62
Experiment	Bending; T: 20°C
Specimen	R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	269.0
Tensile strength (MPa)	407.0
Elongation (%)	9.0
Hardness (HB)	115.0

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

9.薄板; 1.6 mm; Solution heat treated, cold worked and artificially aged (T851); Bending; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	sheet; 1.6 mm; Solution heat treated cold worked and artificially aged (T851)
Experiment	Bending; T: 20°C
Specimen	R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	352.0
Tensile strength (MPa)	455.0
Elongation (%)	10.0
Hardness (HB)	130.0

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

10.Plates; Solution heat treated, cold worked approximately 1 % and artificially aged (T81); Axial; R=0; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 1 % and artificially aged (T81)
Experiment	Axial; R=0; T: 20°C
Specimen	Smooth

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8

11.Plates; Solution heat treated, cold worked approximately 1 % and artificially aged (T81); Axial; R=0; T: 20°C; Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 1 % and artificially aged (T81)
Experiment	Axial; R=0; T: 20°C
Specimen	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8

12.锻件; Solution heat treated, cold worked and artificially aged (T852); Axial; R=0; T: 20°C; Smooth

Test conditions

Item	Detail
Product	forging; Solution heat treated cold worked and artificially aged (T852)
Experiment	Axial; R=0; T: 20°C
Specimen	Smooth

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	370.0
Tensile strength (MPa)	460.0
Elongation (%)	10.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8

13.固溶热处理和人工时效(T6); Completely reversed flexure; R=-1; T: 20°C; flat sheet

Test conditions

Item	Detail
Product	+T6
Experiment	Completely reversed flexure; R=-1; T: 20°C
Specimen	flat sheet

Stress life

No.	Specimen	Cycles
1	flat sheet	5E8

14.固溶和沉淀热处理 (T62); Completely reversed flexure; R=-1; T: 20°C; flat sheet

Test conditions

Item	Detail
Product	+T62
Experiment	Completely reversed flexure; R=-1; T: 20°C
Specimen	flat sheet

Stress life

No.	Specimen	Cycles
1	flat sheet	5E8

15.挤压件，锻件; 固溶热处理和人工时效(T6); Completely reversed bending; R=-1; T: 20°C; Cantilever beam

Test conditions

Item	Detail
Product	extrusion，forging; +T6
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Cantilever beam

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	Cantilever beam		5E8
2	Smooth	R.R. Moore rotating beam
3	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
4	Cantilever beam		5E8
5	Smooth	R.R. Moore rotating beam
6	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
7	Cantilever beam		5E8
8	Smooth	R.R. Moore rotating beam
9	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

16.挤压件，锻件; 固溶热处理和人工时效(T6); Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	extrusion，forging; +T6
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	Cantilever beam		5E8
2	Smooth	R.R. Moore rotating beam
3	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
4	Cantilever beam		5E8
5	Smooth	R.R. Moore rotating beam
6	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
7	Cantilever beam		5E8
8	Smooth	R.R. Moore rotating beam
9	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

17.挤压件，锻件; 固溶热处理和人工时效(T6); Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	extrusion，forging; +T6
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	Cantilever beam		5E8
2	Smooth	R.R. Moore rotating beam
3	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
4	Cantilever beam		5E8
5	Smooth	R.R. Moore rotating beam
6	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
7	Cantilever beam		5E8
8	Smooth	R.R. Moore rotating beam
9	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

18.固溶和沉淀热处理 (T62); Completely reversed; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	+T62
Experiment	Completely reversed; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	289.0
Tensile strength (MPa)	414.0
Elongation (%)	10.0

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

19.Solution heat treated, cold worked approximately 1 % and artificially aged (T81); Completely reversed; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Solution heat treated cold worked approximately 1 % and artificially aged (T81)
Experiment	Completely reversed; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	351.0
Tensile strength (MPa)	455.0
Elongation (%)	10.0

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

20.Solution heat treated, cold worked and artificially aged (T851); Completely reversed; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Solution heat treated cold worked and artificially aged (T851)
Experiment	Completely reversed; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	351.0
Tensile strength (MPa)	455.0
Elongation (%)	10.0

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

21.Extrusions; Solution heat treated, cold worked approximately 1 % and artificially aged (T81); Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Extrusions; Solution heat treated cold worked approximately 1 % and artificially aged (T81)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam

22.Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Completely reversed; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Completely reversed; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Monotonic

Property	Value
Elastic modulus (GPa)	73.0
Yield strength (MPa)	393.0
Tensile strength (MPa)	476.0
Elongation (%)	10.0

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

23.Plates; Solution heat treated, cold worked and artificially aged (T851); 消除应力; Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked and artificially aged (T851); 消除应力
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

24.Plates; Solution heat treated, cold worked and artificially aged (T851); 消除应力; Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked and artificially aged (T851); 消除应力
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

25.薄板; Thickness (mm): 1.524; 固溶和沉淀热处理 (T62); Axial; R=0; T: 20°C; Single V butt weld, 2319 filler, bead-on; 方向: T

Test conditions

Item	Detail
Product	sheet; Thickness (mm): 1.524; +T62
Experiment	Axial; R=0; T: 20°C
Specimen	Single V butt weld 2319 filler bead-on; 方向: T

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	Single V butt weld	2319 filler	bead-on; 方向: T
2	Single V butt weld	2319 filler	bead-off; 方向: T
3	Single V butt weld	2319 filler	bead-on; 方向: T
4	Single V butt weld	2319 filler	bead-off; 方向: T

26.薄板; Thickness (mm): 1.524; 固溶和沉淀热处理 (T62); Axial; R=0; T: 20°C; Single V butt weld, 2319 filler, bead-off; 方向: T

Test conditions

Item	Detail
Product	sheet; Thickness (mm): 1.524; +T62
Experiment	Axial; R=0; T: 20°C
Specimen	Single V butt weld 2319 filler bead-off; 方向: T

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	Single V butt weld	2319 filler	bead-on; 方向: T
2	Single V butt weld	2319 filler	bead-off; 方向: T
3	Single V butt weld	2319 filler	bead-on; 方向: T
4	Single V butt weld	2319 filler	bead-off; 方向: T

27.Plates; Solution heat treated, cold worked approximately 1 % and naturally aged (T31); Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 1 % and naturally aged (T31)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

28.Plates; Solution heat treated, cold worked approximately 1 % and naturally aged (T31); Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 1 % and naturally aged (T31)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

29.挤压件、板材; Solution heat treated and artificially aged (T62); Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	extrusion、plate; Solution heat treated and artificially aged (T62)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

30.挤压件、板材; Solution heat treated and artificially aged (T62); Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	extrusion、plate; Solution heat treated and artificially aged (T62)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

31.Extrusions; Solution heat treated, cold worked approximately 1 % and artificially aged (T81); Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Extrusions; Solution heat treated cold worked approximately 1 % and artificially aged (T81)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

32.Extrusions; Solution heat treated, cold worked approximately 1 % and artificially aged (T81); Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Extrusions; Solution heat treated cold worked approximately 1 % and artificially aged (T81)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

33.Extrusions; 沉淀热处理 (T8511); 消除应力; Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Extrusions; +T8511; stress relieved
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

34.Extrusions; 沉淀热处理 (T8511); 消除应力; Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Extrusions; +T8511; stress relieved
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

35.Plates; Thickness (mm): <= 90; Solution heat treated, cold worked and artificially aged (T852); 消除应力; Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Thickness (mm): <= 90; Solution heat treated cold worked and artificially aged (T852); 消除应力
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam

36.Plates; Solution heat treated, cold worked and artificially aged (T851); Axial; R=0.5; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked and artificially aged (T851)
Experiment	Axial; R=0.5; T: 20°C
Specimen	Smooth

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	345.0
Tensile strength (MPa)	455.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Smooth	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Smooth	5E8
12	Smooth	5E8
13	Smooth	5E8
14	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
15	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
16	Smooth	1E7
17	Smooth	1E7
18	Smooth	1E7
19	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
20	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
21	Smooth	1E8
22	Smooth	1E8
23	Smooth	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

37.Plates; Solution heat treated, cold worked and artificially aged (T851); Axial; R=0; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked and artificially aged (T851)
Experiment	Axial; R=0; T: 20°C
Specimen	Smooth

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	345.0
Tensile strength (MPa)	455.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Smooth	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Smooth	5E8
12	Smooth	5E8
13	Smooth	5E8
14	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
15	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
16	Smooth	1E7
17	Smooth	1E7
18	Smooth	1E7
19	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
20	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
21	Smooth	1E8
22	Smooth	1E8
23	Smooth	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

38.Plates; Solution heat treated, cold worked and artificially aged (T851); Axial; R=-1; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked and artificially aged (T851)
Experiment	Axial; R=-1; T: 20°C
Specimen	Smooth

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	345.0
Tensile strength (MPa)	455.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Smooth	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Smooth	5E8
12	Smooth	5E8
13	Smooth	5E8
14	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
15	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
16	Smooth	1E7
17	Smooth	1E7
18	Smooth	1E7
19	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
20	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
21	Smooth	1E8
22	Smooth	1E8
23	Smooth	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

39.Plates; Solution heat treated, cold worked and artificially aged (T851); Axial; R=0; T: 20°C; Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked and artificially aged (T851)
Experiment	Axial; R=0; T: 20°C
Specimen	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	345.0
Tensile strength (MPa)	455.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Smooth	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Smooth	5E8
12	Smooth	5E8
13	Smooth	5E8
14	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
15	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
16	Smooth	1E7
17	Smooth	1E7
18	Smooth	1E7
19	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
20	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
21	Smooth	1E8
22	Smooth	1E8
23	Smooth	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

40.Plates; Solution heat treated, cold worked and artificially aged (T851); Axial; R=-1; T: 20°C; Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked and artificially aged (T851)
Experiment	Axial; R=-1; T: 20°C
Specimen	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	345.0
Tensile strength (MPa)	455.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Smooth	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Smooth	5E8
12	Smooth	5E8
13	Smooth	5E8
14	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
15	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
16	Smooth	1E7
17	Smooth	1E7
18	Smooth	1E7
19	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
20	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E7
21	Smooth	1E8
22	Smooth	1E8
23	Smooth	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

41.锻件, 厚板; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Completely reversed bending; R=-1; T: 20°C; Smooth, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	forging 厚板; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Smooth R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

42.锻件, 厚板; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Completely reversed bending; R=-1; T: 20°C; Notched, R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	forging 厚板; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Completely reversed bending; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

Stress life

No.	Specimen	Stress (MPa)
1	Smooth	R.R. Moore rotating beam
2	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125
3	Smooth	R.R. Moore rotating beam
4	Notched	R.R. Moore rotating beam; Single 60° sharp V-notch; Deep [mm]: 1.91; Root diameter [mm]: 8.38; Root radius at base of notch [mm]: < 0.0125

43.Plates; 沉淀热处理至回火 T87; Axial; R=0.5; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; tempered T87
Experiment	Axial; R=0.5; T: 20°C
Specimen	Smooth

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	385.0
Tensile strength (MPa)	470.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Smooth	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
12	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
13	Smooth	1E8
14	Smooth	1E8
15	Smooth	1E8
16	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
17	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
18	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
19	Smooth	1E8
20	Smooth	1E8
21	Smooth	1E8
22	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
23	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Smooth	1E8
26	Smooth	1E8
27	Smooth	1E8
28	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
29	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
30	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
31	Smooth	1E8
32	Smooth	1E8
33	Smooth	1E8
34	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
35	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
36	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

44.Plates; 沉淀热处理至回火 T87; Axial; R=0; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; tempered T87
Experiment	Axial; R=0; T: 20°C
Specimen	Smooth

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	385.0
Tensile strength (MPa)	470.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Smooth	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
12	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
13	Smooth	1E8
14	Smooth	1E8
15	Smooth	1E8
16	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
17	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
18	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
19	Smooth	1E8
20	Smooth	1E8
21	Smooth	1E8
22	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
23	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Smooth	1E8
26	Smooth	1E8
27	Smooth	1E8
28	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
29	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
30	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
31	Smooth	1E8
32	Smooth	1E8
33	Smooth	1E8
34	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
35	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
36	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

45.Plates; 沉淀热处理至回火 T87; Axial; R=-1; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; tempered T87
Experiment	Axial; R=-1; T: 20°C
Specimen	Smooth

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	385.0
Tensile strength (MPa)	470.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Smooth	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
12	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
13	Smooth	1E8
14	Smooth	1E8
15	Smooth	1E8
16	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
17	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
18	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
19	Smooth	1E8
20	Smooth	1E8
21	Smooth	1E8
22	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
23	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Smooth	1E8
26	Smooth	1E8
27	Smooth	1E8
28	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
29	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
30	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
31	Smooth	1E8
32	Smooth	1E8
33	Smooth	1E8
34	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
35	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
36	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

46.Plates; 沉淀热处理至回火 T87; Axial; R=0; T: 20°C; Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; tempered T87
Experiment	Axial; R=0; T: 20°C
Specimen	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	385.0
Tensile strength (MPa)	470.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Smooth	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
12	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
13	Smooth	1E8
14	Smooth	1E8
15	Smooth	1E8
16	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
17	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
18	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
19	Smooth	1E8
20	Smooth	1E8
21	Smooth	1E8
22	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
23	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Smooth	1E8
26	Smooth	1E8
27	Smooth	1E8
28	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
29	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
30	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
31	Smooth	1E8
32	Smooth	1E8
33	Smooth	1E8
34	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
35	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
36	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

47.Plates; 沉淀热处理至回火 T87; Axial; R=-1; T: 20°C; Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; tempered T87
Experiment	Axial; R=-1; T: 20°C
Specimen	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	385.0
Tensile strength (MPa)	470.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Smooth	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
12	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
13	Smooth	1E8
14	Smooth	1E8
15	Smooth	1E8
16	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
17	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
18	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
19	Smooth	1E8
20	Smooth	1E8
21	Smooth	1E8
22	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
23	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Smooth	1E8
26	Smooth	1E8
27	Smooth	1E8
28	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
29	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
30	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
31	Smooth	1E8
32	Smooth	1E8
33	Smooth	1E8
34	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
35	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
36	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

48.Plates; 沉淀热处理至回火 T87; Axial; R=0.5; T: 20°C; Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Test conditions

Item	Detail
Product	Plates; tempered T87
Experiment	Axial; R=0.5; T: 20°C
Specimen	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125

Monotonic

Property	Value
Elastic modulus (GPa)	72.0
Yield strength (MPa)	385.0
Tensile strength (MPa)	470.0
Elongation (%)	12.0

Stress life

No.	Specimen	Cycles
1	Smooth	5E8
2	Smooth	5E8
3	Smooth	5E8
4	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
5	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
6	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
7	Smooth	5E8
8	Smooth	5E8
9	Smooth	5E8
10	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
11	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
12	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	5E8
13	Smooth	1E8
14	Smooth	1E8
15	Smooth	1E8
16	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
17	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
18	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
19	Smooth	1E8
20	Smooth	1E8
21	Smooth	1E8
22	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
23	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
24	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
25	Smooth	1E8
26	Smooth	1E8
27	Smooth	1E8
28	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
29	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
30	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
31	Smooth	1E8
32	Smooth	1E8
33	Smooth	1E8
34	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
35	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8
36	Notched; Single 60° sharp V-notch; Deep [mm]: 0.762; Root diameter [mm]: 7.62; Root radius at base of notch [mm]: < 0.0125	1E8

49.锻件; 固溶热处理和人工时效(T6); Completely reversed bending; R=-1; T: 150°C; Cantilever beam

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Completely reversed bending; R=-1; T: 150°C
Specimen	Cantilever beam

Stress life

No.	Specimen	Cycles
1	Cantilever beam	5E8

50.锻件; 固溶热处理和人工时效(T6); Completely reversed bending; R=-1; T: 205°C; Cantilever beam

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Completely reversed bending; R=-1; T: 205°C
Specimen	Cantilever beam

Stress life

No.	Specimen	Cycles
1	Cantilever beam	5E8

51.锻件; 固溶热处理和人工时效(T6); Completely reversed bending; R=-1; T: 260°C; Cantilever beam

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Completely reversed bending; R=-1; T: 260°C
Specimen	Cantilever beam

Stress life

No.	Specimen	Cycles
1	Cantilever beam	5E8

52.锻件; 固溶热处理和人工时效(T6); Completely reversed bending; R=-1; T: 315°C; Cantilever beam

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Completely reversed bending; R=-1; T: 315°C
Specimen	Cantilever beam

Stress life

No.	Specimen	Cycles
1	Cantilever beam	5E8

53.锻件; 固溶热处理和人工时效(T6); Rotating beam; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Rotating beam; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	1E8

54.锻件; 固溶热处理和人工时效(T6); Cantilever bending; R=-1; T: 150°C; Notched

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Cantilever bending; R=-1; T: 150°C
Specimen	Notched

Stress life

No.	Specimen	Cycles
1	Notched	5E8

55.锻件; 固溶热处理和人工时效(T6); Cantilever bending; R=-1; T: 200°C; Unnotched

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Cantilever bending; R=-1; T: 200°C
Specimen	Unnotched

Stress life

No.	Specimen	Cycles
1	Unnotched	5E8

56.锻件; 固溶热处理和人工时效(T6); Cantilever bending; R=-1; T: 260°C; Notched

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Cantilever bending; R=-1; T: 260°C
Specimen	Notched

Stress life

No.	Specimen	Cycles
1	Notched	5E8

57.锻件; 固溶热处理和人工时效(T6); Cantilever bending; R=-1; T: 315°C; Unnotched

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Cantilever bending; R=-1; T: 315°C
Specimen	Unnotched

Stress life

No.	Specimen	Cycles
1	Unnotched	1E8
2	Notched	1E8
3	Unnotched	5E8
4	Notched	5E8

58.锻件; 固溶热处理和人工时效(T6); Cantilever bending; R=-1; T: 315°C; Notched

Test conditions

Item	Detail
Product	forging; +T6
Experiment	Cantilever bending; R=-1; T: 315°C
Specimen	Notched

Stress life

No.	Specimen	Cycles
1	Unnotched	1E8
2	Notched	1E8
3	Unnotched	5E8
4	Notched	5E8

59.Plates; Solution heat treated and artificially aged (T62); Axial; R=0; T: 20°C; round

Test conditions

Item	Detail
Product	Plates; Solution heat treated and artificially aged (T62)
Experiment	Axial; R=0; T: 20°C
Specimen	round

Stress life

No.	Specimen	Cycles
1	round	1E8

60.Plates; Solution heat treated, cold worked approximately 1 % and naturally aged (T31); Rotating beam; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 1 % and naturally aged (T31)
Experiment	Rotating beam; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

61.Plates; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Rotating beam; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Rotating beam; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Smooth		5E8
3	Smooth		5E8
4	Smooth		5E8
5	Notched	R.R. Moore rotating beam
6	round		5E8
7	Round notch		5E8
8	R.R. Moore rotating beam		5E8
9	Smooth		5E8
10	Smooth		5E8
11	Smooth		5E8
12	Notched	R.R. Moore rotating beam
13	round		5E8
14	Round notch		5E8
15	R.R. Moore rotating beam		5E8
16	Smooth		5E8
17	Smooth		5E8
18	Smooth		5E8
19	Notched	R.R. Moore rotating beam
20	round		5E8
21	Round notch		5E8
22	R.R. Moore rotating beam		1E8
23	Smooth		1E8
24	Smooth		1E8
25	Smooth		1E8
26	Notched	R.R. Moore rotating beam
27	round		1E8
28	Round notch		1E8
29	R.R. Moore rotating beam		5E8
30	Smooth		5E8
31	Smooth		5E8
32	Smooth		5E8
33	Notched	R.R. Moore rotating beam
34	round		5E8
35	Round notch		5E8
36	R.R. Moore rotating beam		1E8
37	Smooth		1E8
38	Smooth		1E8
39	Smooth		1E8
40	Notched	R.R. Moore rotating beam
41	round		1E8
42	Round notch		1E8
43	R.R. Moore rotating beam		1E8
44	Smooth		1E8
45	Smooth		1E8
46	Smooth		1E8
47	Notched	R.R. Moore rotating beam
48	round		1E8
49	Round notch		1E8

62.Plates; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Axial; R=0.5; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Axial; R=0.5; T: 20°C
Specimen	Smooth

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Smooth		5E8
3	Smooth		5E8
4	Smooth		5E8
5	Notched	R.R. Moore rotating beam
6	round		5E8
7	Round notch		5E8
8	R.R. Moore rotating beam		5E8
9	Smooth		5E8
10	Smooth		5E8
11	Smooth		5E8
12	Notched	R.R. Moore rotating beam
13	round		5E8
14	Round notch		5E8
15	R.R. Moore rotating beam		5E8
16	Smooth		5E8
17	Smooth		5E8
18	Smooth		5E8
19	Notched	R.R. Moore rotating beam
20	round		5E8
21	Round notch		5E8
22	R.R. Moore rotating beam		1E8
23	Smooth		1E8
24	Smooth		1E8
25	Smooth		1E8
26	Notched	R.R. Moore rotating beam
27	round		1E8
28	Round notch		1E8
29	R.R. Moore rotating beam		5E8
30	Smooth		5E8
31	Smooth		5E8
32	Smooth		5E8
33	Notched	R.R. Moore rotating beam
34	round		5E8
35	Round notch		5E8
36	R.R. Moore rotating beam		1E8
37	Smooth		1E8
38	Smooth		1E8
39	Smooth		1E8
40	Notched	R.R. Moore rotating beam
41	round		1E8
42	Round notch		1E8
43	R.R. Moore rotating beam		1E8
44	Smooth		1E8
45	Smooth		1E8
46	Smooth		1E8
47	Notched	R.R. Moore rotating beam
48	round		1E8
49	Round notch		1E8

63.Plates; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Axial; R=0; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Axial; R=0; T: 20°C
Specimen	Smooth

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Smooth		5E8
3	Smooth		5E8
4	Smooth		5E8
5	Notched	R.R. Moore rotating beam
6	round		5E8
7	Round notch		5E8
8	R.R. Moore rotating beam		5E8
9	Smooth		5E8
10	Smooth		5E8
11	Smooth		5E8
12	Notched	R.R. Moore rotating beam
13	round		5E8
14	Round notch		5E8
15	R.R. Moore rotating beam		5E8
16	Smooth		5E8
17	Smooth		5E8
18	Smooth		5E8
19	Notched	R.R. Moore rotating beam
20	round		5E8
21	Round notch		5E8
22	R.R. Moore rotating beam		1E8
23	Smooth		1E8
24	Smooth		1E8
25	Smooth		1E8
26	Notched	R.R. Moore rotating beam
27	round		1E8
28	Round notch		1E8
29	R.R. Moore rotating beam		5E8
30	Smooth		5E8
31	Smooth		5E8
32	Smooth		5E8
33	Notched	R.R. Moore rotating beam
34	round		5E8
35	Round notch		5E8
36	R.R. Moore rotating beam		1E8
37	Smooth		1E8
38	Smooth		1E8
39	Smooth		1E8
40	Notched	R.R. Moore rotating beam
41	round		1E8
42	Round notch		1E8
43	R.R. Moore rotating beam		1E8
44	Smooth		1E8
45	Smooth		1E8
46	Smooth		1E8
47	Notched	R.R. Moore rotating beam
48	round		1E8
49	Round notch		1E8

64.Plates; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Axial; R=-1; T: 20°C; Smooth

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Axial; R=-1; T: 20°C
Specimen	Smooth

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Smooth		5E8
3	Smooth		5E8
4	Smooth		5E8
5	Notched	R.R. Moore rotating beam
6	round		5E8
7	Round notch		5E8
8	R.R. Moore rotating beam		5E8
9	Smooth		5E8
10	Smooth		5E8
11	Smooth

65.Plates; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Rotating beam; R=-1; T: 20°C; Notched, R.R. Moore rotating beam

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Rotating beam; R=-1; T: 20°C
Specimen	Notched R.R. Moore rotating beam

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Smooth		5E8
3	Smooth		5E8
4	Smooth		5E8
5	Notched	R.R. Moore rotating beam
6	round		5E8
7	Round notch		5E8
8	R.R. Moore rotating beam		5E8
9	Smooth		5E8
10	Smooth		5E8
11	Smooth		5E8
12	Notched	R.R. Moore rotating beam
13	round		5E8
14	Round notch		5E8
15	R.R. Moore rotating beam		5E8
16	Smooth		5E8
17	Smooth		5E8
18	Smooth		5E8
19	Notched	R.R. Moore rotating beam
20	round		5E8
21	Round notch		5E8
22	R.R. Moore rotating beam		1E8
23	Smooth		1E8
24	Smooth		1E8
25	Smooth		1E8
26	Notched	R.R. Moore rotating beam
27	round		1E8
28	Round notch		1E8
29	R.R. Moore rotating beam		5E8
30	Smooth		5E8
31	Smooth		5E8
32	Smooth		5E8
33	Notched	R.R. Moore rotating beam
34	round		5E8
35	Round notch		5E8
36	R.R. Moore rotating beam		1E8
37	Smooth		1E8
38	Smooth		1E8
39	Smooth		1E8
40	Notched	R.R. Moore rotating beam
41	round		1E8
42	Round notch		1E8
43	R.R. Moore rotating beam		1E8
44	Smooth		1E8
45	Smooth		1E8
46	Smooth		1E8
47	Notched	R.R. Moore rotating beam
48	round		1E8
49	Round notch		1E8

66.Plates; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Axial; R=-1; T: 20°C; round

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Axial; R=-1; T: 20°C
Specimen	round

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Smooth		5E8
3	Smooth		5E8
4	Smooth		5E8
5	Notched	R.R. Moore rotating beam
6	round		5E8
7	Round notch		5E8
8	R.R. Moore rotating beam		5E8
9	Smooth		5E8
10	Smooth		5E8
11	Smooth		5E8
12	Notched	R.R. Moore rotating beam
13	round		5E8
14	Round notch		5E8
15	R.R. Moore rotating beam		5E8
16	Smooth		5E8
17	Smooth		5E8
18	Smooth		5E8
19	Notched	R.R. Moore rotating beam
20	round		5E8
21	Round notch		5E8
22	R.R. Moore rotating beam		1E8
23	Smooth		1E8
24	Smooth		1E8
25	Smooth		1E8
26	Notched	R.R. Moore rotating beam
27	round		1E8
28	Round notch		1E8
29	R.R. Moore rotating beam		5E8
30	Smooth		5E8
31	Smooth		5E8
32	Smooth		5E8
33	Notched	R.R. Moore rotating beam
34	round		5E8
35	Round notch		5E8
36	R.R. Moore rotating beam		1E8
37	Smooth		1E8
38	Smooth		1E8
39	Smooth		1E8
40	Notched	R.R. Moore rotating beam
41	round		1E8
42	Round notch		1E8
43	R.R. Moore rotating beam		1E8
44	Smooth		1E8
45	Smooth		1E8
46	Smooth		1E8
47	Notched	R.R. Moore rotating beam
48	round		1E8
49	Round notch		1E8

67.Plates; Solution heat treated, cold worked approximately 7 % and artificially aged (T87); Axial; R=-1; T: 20°C; Round notch

Test conditions

Item	Detail
Product	Plates; Solution heat treated cold worked approximately 7 % and artificially aged (T87)
Experiment	Axial; R=-1; T: 20°C
Specimen	Round notch

Stress life

No.	Specimen	Stress (MPa)	Cycles
1	R.R. Moore rotating beam		5E8
2	Smooth		5E8
3	Smooth		5E8
4	Smooth		5E8
5	Notched	R.R. Moore rotating beam
6	round		5E8
7	Round notch		5E8
8	R.R. Moore rotating beam		5E8
9	Smooth		5E8
10	Smooth		5E8
11	Smooth		5E8
12	Notched	R.R. Moore rotating beam
13	round		5E8
14	Round notch		5E8
15	R.R. Moore rotating beam		5E8
16	Smooth		5E8
17	Smooth		5E8
18	Smooth		5E8
19	Notched	R.R. Moore rotating beam
20	round		5E8
21	Round notch		5E8
22	R.R. Moore rotating beam		1E8
23	Smooth		1E8
24	Smooth		1E8
25	Smooth		1E8
26	Notched	R.R. Moore rotating beam
27	round		1E8
28	Round notch		1E8
29	R.R. Moore rotating beam		5E8
30	Smooth		5E8
31	Smooth		5E8
32	Smooth		5E8
33	Notched	R.R. Moore rotating beam
34	round		5E8
35	Round notch		5E8
36	R.R. Moore rotating beam		1E8
37	Smooth		1E8
38	Smooth		1E8
39	Smooth		1E8
40	Notched	R.R. Moore rotating beam
41	round		1E8
42	Round notch		1E8
43	R.R. Moore rotating beam		1E8
44	Smooth		1E8
45	Smooth		1E8
46	Smooth		1E8
47	Notched	R.R. Moore rotating beam
48	round		1E8
49	Round notch		1E8

68.钢棒; Solution heat treated, cold worked approximately 1 % and naturally aged (T31); Rotating beam; R=-1; T: 20°C; R.R. Moore rotating beam

Test conditions

Item	Detail
Product	steel bar; Solution heat treated cold worked approximately 1 % and naturally aged (T31)
Experiment	Rotating beam; R=-1; T: 20°C
Specimen	R.R. Moore rotating beam

Stress life

No.	Specimen	Cycles
1	R.R. Moore rotating beam	5E8

Creep

Condition

1.Annealed (O)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
25	0.1h	170.0	170.0	150.0	130.0	170.0
25	1.0h	170.0	165.0	145.0	125.0	170.0
25	10.0h	170.0	160.0	140.0	110.0	170.0
25	100.0h	165.0	150.0	130.0	105.0	170.0
25	1000.0h	150.0	140.0	125.0	95.0	170.0

2.Solution heat treated, cold worked approximately 7 % and naturally aged (T37)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
25	0.1h	170.0	170.0	150.0	130.0	170.0
25	1.0h	170.0	165.0	145.0	125.0	170.0
25	10.0h	170.0	160.0	140.0	110.0	170.0
25	100.0h	165.0	150.0	130.0	105.0	170.0
25	1000.0h	150.0	140.0	125.0	95.0	170.0

3.Solution heat treated, cold worked approximately 7 % and naturally aged (T37)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
260	0.1h	165.0	150.0	140.0	115.0	170.0
260	1.0h	145.0	130.0	110.0	90.0	150.0
260	10.0h	115.0	105.0	85.0		125.0
260	100.0h	85.0	75.0			90.0
315	0.1h	115.0	110.0	95.0	85.0	125.0
315	1.0h	95.0	85.0	70.0	55.0	105.0
315	10.0h	59.0	52.0			70.0

4.Solution heat treated and artificially aged, 18h at 190 °C (T6)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
260	0.1h	165.0	150.0	140.0	115.0	170.0
260	1.0h	145.0	130.0	110.0	90.0	150.0
260	10.0h	115.0	105.0	85.0		125.0
260	100.0h	85.0	75.0			90.0
315	0.1h	115.0	110.0	95.0	85.0	125.0
315	1.0h	95.0	85.0	70.0	55.0	105.0
315	10.0h	59.0	52.0			70.0

5.固溶热处理和人工时效16h 在 215°C (T6)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
25	0.1h	420.0	405.0	345.0	290.0	435.0
25	1.0h	405.0	385.0	310.0	270.0	425.0
25	10.0h	400.0	345.0	290.0	260.0	420.0
25	100.0h	380.0	330.0	275.0	255.0	405.0
25	1000.0h	345.0	325.0	270.0	250.0	400.0
100	0.1h	345.0	310.0	260.0	235.0	370.0
100	1.0h	315.0	275.0	250.0	230.0	350.0
100	10.0h	295.0	260.0	235.0	220.0	340.0
100	100.0h	275.0	255.0	220.0	220.0	325.0
100	1000.0h	270.0	250.0	220.0	215.0	310.0
205	0.1h	235.0	230.0	220.0	205.0	255.0
205	1.0h	205.0	195.0	185.0	165.0	235.0
205	10.0h	180.0	160.0	105.0	59.0	205.0
205	100.0h	165.0	140.0	75.0	32.0	185.0
205	1000.0h	140.0	125.0	62.0	23.0	160.0
260	0.1h	160.0	145.0	130.0	115.0	180.0
260	1.0h	145.0	130.0	115.0	95.0	160.0
260	10.0h	125.0	110.0	95.0	85.0	140.0
260	100.0h	110.0	95.0	85.0	70.0	115.0
260	1000.0h	95.0	85.0	66.0	59.0	95.0
315	0.1h	110.0	105.0	90.0	75.0	125.0
315	1.0h	95.0	85.0	70.0	55.0	105.0
315	10.0h	75.0	66.0	52.0	38.0	85.0
315	100.0h	52.0	48.0	34.0	23.0	62.0
315	1000.0h	38.0	32.0	21.0	15.0	45.0
370	0.1h	52.0	48.0	45.0	34.0	59.0
370	1.0h	45.0	41.0	32.0	17.0	48.0
370	10.0h	30.0	26.0	17.0	12.0	34.0
370	100.0h	20.0	17.0	11.0	8.0	23.0
370	1000.0h	13.0	11.0	8.0	6.0	17.0

6.固溶和沉淀热处理 (T62)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
25	0.1h	420.0	405.0	345.0	290.0	435.0
25	1.0h	405.0	385.0	310.0	270.0	425.0
25	10.0h	400.0	345.0	290.0	260.0	420.0
25	100.0h	380.0	330.0	275.0	255.0	405.0
25	1000.0h	345.0	325.0	270.0	250.0	400.0
100	0.1h	345.0	310.0	260.0	235.0	370.0
100	1.0h	315.0	275.0	250.0	230.0	350.0
100	10.0h	295.0	260.0	235.0	220.0	340.0
100	100.0h	275.0	255.0	220.0	220.0	325.0
100	1000.0h	270.0	250.0	220.0	215.0	310.0
205	0.1h	235.0	230.0	220.0	205.0	255.0
205	1.0h	205.0	195.0	185.0	165.0	235.0
205	10.0h	180.0	160.0	105.0	59.0	205.0
205	100.0h	165.0	140.0	75.0	32.0	185.0
205	1000.0h	140.0	125.0	62.0	23.0	160.0
260	0.1h	160.0	145.0	130.0	115.0	180.0
260	1.0h	145.0	130.0	115.0	95.0	160.0
260	10.0h	125.0	110.0	95.0	85.0	140.0
260	100.0h	110.0	95.0	85.0	70.0	115.0
260	1000.0h	95.0	85.0	66.0	59.0	95.0
315	0.1h	110.0	105.0	90.0	75.0	125.0
315	1.0h	95.0	85.0	70.0	55.0	105.0
315	10.0h	75.0	66.0	52.0	38.0	85.0
315	100.0h	52.0	48.0	34.0	23.0	62.0
315	1000.0h	38.0	32.0	21.0	15.0	45.0
370	0.1h	52.0	48.0	45.0	34.0	59.0
370	1.0h	45.0	41.0	32.0	17.0	48.0
370	10.0h	30.0	26.0	17.0	12.0	34.0
370	100.0h	20.0	17.0	11.0	8.0	23.0
370	1000.0h	13.0	11.0	8.0	6.0	17.0

7.固溶和沉淀热处理 (T62)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
100	0.1h	330.0	315.0			360.0
100	1.0h					340.0
100	10.0h					315.0
150	0.1h	255.0	234.0	214.0	200.0	303.0
150	1.0h	235.0	220.0	200.0	185.0	275.0
150	10.0h	220.0	205.0	185.0	170.0	255.0
150	100.0h	205.0	185.0	165.0	140.0	235.0
150	1000.0h	195.0	170.0	125.0	110.0	200.0
205	0.1h	200.0	185.0	170.0	160.0	235.0
205	1.0h	180.0	165.0	150.0	130.0	205.0
205	10.0h	160.0	150.0	125.0	105.0	180.0
205	100.0h	130.0	115.0	90.0	66.0	145.0
205	1000.0h	95.0	85.0	66.0	48.0	105.0
230	0.1h	170.0	160.0	145.0	130.0	200.0
230	1.0h	150.0	140.0	115.0	105.0	170.0
230	10.0h	125.0	115.0	90.0	69.0	145.0
230	100.0h	95.0	85.0	59.0	41.0	105.0
230	1000.0h	59.0	52.0	41.0	28.0	66.0
260	0.1h	145.0	140.0	115.0	103.0	165.0
260	1.0h	125.0	110.0	90.0	75.0	140.0
260	10.0h	95.0	85.0	55.0	48.0	105.0
260	100.0h	62.0	52.0	41.0	27.0	70.0
260	1000.0h	34.0	30.0	23.0	18.0	41.0
290	0.1h	125.0	115.0	105.0	85.0	140.0
290	1.0h	105.0	90.0	70.0	55.0	110.0
290	10.0h	66.0	55.0	38.0	32.0	75.0
290	100.0h	41.0	34.0	28.0	19.0	52.0
290	1000.0h	24.0	21.0	17.0	12.0	28.0
315	0.1h	105.0	95.0	85.0	70.0	110.0
315	1.0h	85.0	70.0	52.0	38.0	90.0
315	10.0h	48.0	38.0	28.0	23.0	55.0
315	100.0h	30.0	26.0	19.0	14.0	38.0
315	1000.0h	18.0	15.0	12.0	8.0	22.0
370	0.1h	69.0	62.0	52.0	34.0	70.0
370	1.0h	48.0	45.0	32.0	18.0	55.0
370	10.0h	30.0	26.0	17.0	12.0	34.0
370	100.0h	20.0	17.0	11.0	8.0	23.0
370	1000.0h	13.0	11.0	8.0	6.0	17.0

8.Solution heat treated, cold worked approximately 1 % and artificially aged (T81)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
100	0.1h	330.0	315.0			360.0
100	1.0h					340.0
100	10.0h					315.0
150	0.1h	255.0	234.0	214.0	200.0	303.0
150	1.0h	235.0	220.0	200.0	185.0	275.0
150	10.0h	220.0	205.0	185.0	170.0	255.0
150	100.0h	205.0	185.0	165.0	140.0	235.0
150	1000.0h	195.0	170.0	125.0	110.0	200.0
205	0.1h	200.0	185.0	170.0	160.0	235.0
205	1.0h	180.0	165.0	150.0	130.0	205.0
205	10.0h	160.0	150.0	125.0	105.0	180.0
205	100.0h	130.0	115.0	90.0	66.0	145.0
205	1000.0h	95.0	85.0	66.0	48.0	105.0
230	0.1h	170.0	160.0	145.0	130.0	200.0
230	1.0h	150.0	140.0	115.0	105.0	170.0
230	10.0h	125.0	115.0	90.0	69.0	145.0
230	100.0h	95.0	85.0	59.0	41.0	105.0
230	1000.0h	59.0	52.0	41.0	28.0	66.0
260	0.1h	145.0	140.0	115.0	103.0	165.0
260	1.0h	125.0	110.0	90.0	75.0	140.0
260	10.0h	95.0	85.0	55.0	48.0	105.0
260	100.0h	62.0	52.0	41.0	27.0	70.0
260	1000.0h	34.0	30.0	23.0	18.0	41.0
290	0.1h	125.0	115.0	105.0	85.0	140.0
290	1.0h	105.0	90.0	70.0	55.0	110.0
290	10.0h	66.0	55.0	38.0	32.0	75.0
290	100.0h	41.0	34.0	28.0	19.0	52.0
290	1000.0h	24.0	21.0	17.0	12.0	28.0
315	0.1h	105.0	95.0	85.0	70.0	110.0
315	1.0h	85.0	70.0	52.0	38.0	90.0
315	10.0h	48.0	38.0	28.0	23.0	55.0
315	100.0h	30.0	26.0	19.0	14.0	38.0
315	1000.0h	18.0	15.0	12.0	8.0	22.0
370	0.1h	69.0	62.0	52.0	34.0	70.0
370	1.0h	48.0	45.0	32.0	18.0	55.0
370	10.0h	30.0	26.0	17.0	12.0	34.0
370	100.0h	20.0	17.0	11.0	8.0	23.0
370	1000.0h	13.0	11.0	8.0	6.0	17.0

9.Solution heat treated, cold worked and artificially aged (T851)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
150	0.1h	305.0	290.0	275.0	260.0	340.0
150	1.0h	285.0	275.0	255.0	230.0	310.0
150	10.0h	260.0	255.0	230.0	185.0	275.0
150	100.0h	240.0	230.0	185.0	150.0	250.0
150	1000.0h	200.0	185.0	150.0	125.0	205.0
205	0.1h	240.0	230.0	205.0	180.0	255.0
205	1.0h	205.0	195.0	170.0	145.0	230.0
205	10.0h	180.0	165.0	140.0	105.0	185.0
205	100.0h	150.0	130.0	95.0	62.0	150.0
205	1000.0h	95.0	85.0	70.0	48.0	105.0
230	0.1h	200.0	185.0	165.0	145.0	215.0
230	1.0h	170.0	165.0	140.0	110.0	185.0
230	10.0h	140.0	130.0	105.0	75.0	150.0
230	100.0h	110.0	90.0	70.0	52.0	110.0
230	1000.0h	66.0	62.0	55.0	38.0	70.0
260	0.1h	160.0	150.0	140.0	115.0	170.0
260	1.0h	140.0	130.0	105.0	85.0	150.0
260	10.0h	105.0	95.0	75.0	55.0	115.0
260	100.0h	75.0	66.0	55.0	41.0	85.0
260	1000.0h	48.0	48.0	45.0	30.0	48.0
290	0.1h	130.0	125.0	110.0	95.0	140.0
290	1.0h	110.0	105.0	85.0	62.0	125.0
290	10.0h	75.0	66.0	52.0	45.0	90.0
290	100.0h	55.0	48.0	41.0	32.0	62.0
290	1000.0h	34.0	34.0	34.0	23.0	38.0
315	0.1h	110.0	105.0	90.0	75.0	115.0
315	1.0h	90.0	85.0	66.0	48.0	95.0
315	10.0h	55.0	48.0	38.0	32.0	70.0
315	100.0h	41.0	34.0	30.0	24.0	48.0
315	1000.0h	26.0	26.0	26.0	17.0	29.0
370	0.1h	70.0	62.0	52.0	34.0	70.0
370	1.0h	48.0	45.0	32.0	18.0	55.0
370	10.0h	30.0	26.0	17.0	12.0	34.0
370	100.0h	20.0	17.0	11.0	8.0	23.0
370	1000.0h	13.0	11.0	8.0	6.0	17.0

10.Solution heat treated, cold worked and artificially aged (T8511)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
150	0.1h	305.0	290.0	275.0	260.0	340.0
150	1.0h	285.0	275.0	255.0	230.0	310.0
150	10.0h	260.0	255.0	230.0	185.0	275.0
150	100.0h	240.0	230.0	185.0	150.0	250.0
150	1000.0h	200.0	185.0	150.0	125.0	205.0
205	0.1h	240.0	230.0	205.0	180.0	255.0
205	1.0h	205.0	195.0	170.0	145.0	230.0
205	10.0h	180.0	165.0	140.0	105.0	185.0
205	100.0h	150.0	130.0	95.0	62.0	150.0
205	1000.0h	95.0	85.0	70.0	48.0	105.0
230	0.1h	200.0	185.0	165.0	145.0	215.0
230	1.0h	170.0	165.0	140.0	110.0	185.0
230	10.0h	140.0	130.0	105.0	75.0	150.0
230	100.0h	110.0	90.0	70.0	52.0	110.0
230	1000.0h	66.0	62.0	55.0	38.0	70.0
260	0.1h	160.0	150.0	140.0	115.0	170.0
260	1.0h	140.0	130.0	105.0	85.0	150.0
260	10.0h	105.0	95.0	75.0	55.0	115.0
260	100.0h	75.0	66.0	55.0	41.0	85.0
260	1000.0h	48.0	48.0	45.0	30.0	48.0
290	0.1h	130.0	125.0	110.0	95.0	140.0
290	1.0h	110.0	105.0	85.0	62.0	125.0
290	10.0h	75.0	66.0	52.0	45.0	90.0
290	100.0h	55.0	48.0	41.0	32.0	62.0
290	1000.0h	34.0	34.0	34.0	23.0	38.0
315	0.1h	110.0	105.0	90.0	75.0	115.0
315	1.0h	90.0	85.0	66.0	48.0	95.0
315	10.0h	55.0	48.0	38.0	32.0	70.0
315	100.0h	41.0	34.0	30.0	24.0	48.0
315	1000.0h	26.0	26.0	26.0	17.0	29.0
370	0.1h	70.0	62.0	52.0	34.0	70.0
370	1.0h	48.0	45.0	32.0	18.0	55.0
370	10.0h	30.0	26.0	17.0	12.0	34.0
370	100.0h	20.0	17.0	11.0	8.0	23.0
370	1000.0h	13.0	11.0	8.0	6.0	17.0

11.Solution heat treated, cold worked and artificially aged (T852)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
205	0.1h	250.0	235.0	220.0	205.0	260.0
205	1.0h	220.0	215.0	200.0	180.0	240.0
205	10.0h	200.0	195.0	170.0	145.0	215.0
205	100.0h	180.0	170.0	145.0	125.0	185.0
205	1000.0h	150.0	145.0	125.0	105.0	150.0
260	0.1h	180.0	170.0	160.0	145.0	185.0
260	1.0h	165.0	160.0	140.0	125.0	170.0
260	10.0h	145.0	140.0	115.0		150.0
260	100.0h	125.0	115.0			130.0
260	1000.0h	105.0				105.0

12.Solution heat treated, cold worked approximately 7 % and artificially aged (T87)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
205	0.1h	250.0	235.0	220.0	205.0	260.0
205	1.0h	220.0	215.0	200.0	180.0	240.0
205	10.0h	200.0	195.0	170.0	145.0	215.0
205	100.0h	180.0	170.0	145.0	125.0	185.0
205	1000.0h	150.0	145.0	125.0	105.0	150.0
260	0.1h	180.0	170.0	160.0	145.0	185.0
260	1.0h	165.0	160.0	140.0	125.0	170.0
260	10.0h	145.0	140.0	115.0		150.0
260	100.0h	125.0	115.0			130.0
260	1000.0h	105.0				105.0

13.Solution heat treated, cold worked approximately 7 % and artificially aged (T87)

Temperature ℃	Time h	Rp1	Rp0.5	Rp0.2	Rp0.1	CRS
150	0.1h	325.0	315.0	295.0	270.0	350.0
150	1.0h	305.0	290.0	270.0	235.0	325.0
150	10.0h	285.0	270.0	235.0	185.0	295.0
150	100.0h	250.0	235.0	185.0	150.0	255.0
150	1000.0h	200.0	185.0	150.0	125.0	205.0
205	0.1h	250.0	235.0	205.0	180.0	260.0
205	1.0h	220.0	205.0	170.0	145.0	235.0
205	10.0h	185.0	170.0	140.0	105.0	195.0
205	100.0h	150.0	130.0	95.0	62.0	150.0
205	1000.0h	95.0	85.0	70.0	48.0	105.0
230	0.1h	200.0	185.0	165.0	145.0	220.0
230	1.0h	170.0	165.0	140.0	110.0	195.0
230	10.0h	145.0	130.0	105.0	75.0	150.0
230	100.0h	110.0	95.0	75.0	52.0	115.0
230	1000.0h	70.0	66.0	55.0	38.0	75.0
260	0.1h	160.0	150.0	140.0	115.0	170.0
260	1.0h	145.0	130.0	110.0	85.0	150.0
260	10.0h	115.0	105.0	85.0	55.0	125.0
260	100.0h	90.0	75.0	59.0	41.0	90.0
260	1000.0h	52.0	48.0	45.0	30.0	55.0
290	0.1h	140.0	130.0	110.0	95.0	145.0
290	1.0h	115.0	110.0	90.0	70.0	125.0
290	10.0h	90.0	75.0	62.0	45.0	95.0
290	100.0h	66.0	55.0	45.0	32.0	70.0
290	1000.0h	38.0	34.0	34.0	23.0	38.0
315	0.1h	110.0	105.0	90.0	85.0	115.0
315	1.0h	90.0	85.0	70.0	55.0	95.0
315	10.0h	59.0	52.0	45.0	32.0	70.0
315	100.0h	45.0	38.0	32.0	24.0	48.0
315	1000.0h	26.0	26.0	26.0	17.0	29.0
370	0.1h	45.0	45.0	41.0	34.0	45.0
370	1.0h	34.0	34.0	32.0	18.0	41.0
370	10.0h	26.0	21.0	17.0	12.0	30.0
370	100.0h	20.0	17.0	11.0	8.0	23.0
370	1000.0h	13.0	11.0	8.0	6.0	17.0

Similar grades

Grade	Region	System
AL-P2219	European Union	EN
2219	United States	AMS
2219	United States	SAE