欧盟 · EN

CuSn11P-C

EN 1982:2008 — 铜及铜合金 - 铸锭和铸件

化学成分

wt% · 对数刻度
0.0010.010.11101001000Al0.01Cu87 – 89.3Fe0.1Mn0.05Ni0.1P0.6 – 1Pb0.25S0.05Sb0.05Si0.01Sn10.2 – 11.5Zn0.05
  • min – max 范围
  • 典型值

力学性能

按热处理状态分组
屈服强度 Rp0.2≥170 MPa抗拉强度 Rm≥330 MPa伸长率 A≥4 %硬度HBCentrifugal castings (GZ)屈服强度 Rp0.2≥170 MPa抗拉强度 Rm≥310 MPa伸长率 A≥2 %硬度HBPermanent mould castings (GM)屈服强度 Rp0.2≥130 MPa抗拉强度 Rm≥250 MPa伸长率 A≥5 %硬度HBSand castings (GS)屈服强度 Rp0.2≥170 MPa抗拉强度 Rm≥350 MPa伸长率 A≥5 %硬度HB圆钢

化学成分

ElementminmaxSimilarRemarks
Al0.01
Cu8789.3for ingots; for castings 87 < %Cu < 89.5
Fe0.1
Mn0.05
Ni0.1
P0.61for ingots; for castings 0.5 < %P < 1; for sand castings for non-bearing applications the P may be restricted to 0.15% maximum
Pb0.25
S0.05
Sb0.05
Si0.01
Sn10.211.5for ingots; for castings 10 < %Sn < 11.5
Zn0.05

力学性能

热处理 / 状态屈服强度抗拉强度伸长率断面收缩率冲击功硬度
Centrifugal castings (GZ)≥170≥330≥4HB ≥85 HBW
Permanent mould castings (GM)≥170≥310≥2HB ≥85 HBW
Sand castings (GS)≥130≥250≥5HB ≥60 HBW
圆钢≥170≥350≥5HB ≥85 HBW