C 7250 PS
JIS H3100:2012 — 铜及铜合金薄板，板材和条带
化学成分
wt% · 对数刻度- min – max 范围
- 典型值
力学性能
按热处理状态分组化学成分
| Element | min | max | Similar | Remarks |
|---|---|---|---|---|
| Cu | Residual | |||
| Cu+Pb+Fe+Sn+Zn+Mn+Ni | 99.8 | |||
| Fe | 0.6 | |||
| Mn | 0.2 | |||
| Ni | 8.5 | 10.5 | ||
| Pb | 0.05 | |||
| Sn | 1.8 | 2.8 | ||
| Zn | 0.5 |
力学性能
| 热处理 / 状态 | 屈服强度 | 抗拉强度 | 伸长率 | 断面收缩率 | 冲击功 | 硬度 |
|---|---|---|---|---|---|---|
| Plates t-厚度0.15~1mm 半硬(1/2H) | 410–550 | ≥9 | HV 115–180 For t >= 0.10mm; Informative only. | |||
| Plates t-厚度0.15~1mm 硬 | 465–625 | ≥7 | HV 140–210 For t >= 0.10mm; Informative only. | |||
| Plates t-厚度0.1~0.15mm 半硬(1/2H) | 410–550 | ≥5 | HV 115–180 For t >= 0.10mm; Informative only. | |||
| Plates t-厚度0.1~0.15mm 硬 | 465–625 | ≥5 | HV 140–210 For t >= 0.10mm; Informative only. | |||
| Plates t-厚度0.1~1mm Annealed (O) | ≥30 | |||||
| Plates t-厚度0.1~1mm Cold rolled or drawn - 1/4 hard (1/4 H) | HV 85–170 | |||||
| Plates t-厚度0.1~1mm Extra spring hardened (ESH) | HV 185–240 For t >= 0.10mm; Informative only. | |||||
| Plates t-厚度0.1~1mm Spring hardened (SH) | HV 170–230 For t >= 0.10mm; Informative only. | |||||
| Plates t-厚度0.1~1mm Super spring hardened (SSH) | HV ≥220 For t >= 0.10mm; Informative only. | |||||
| Plates t-厚度0.1~1mm 超硬化 (EH) | HV 160–220 For t >= 0.10mm; Informative only. | |||||
| Plates t-厚度0.1~1mm Annealed (O) | HV ≤120 For t >= 0.20mm; Informative only. | |||||
| Plates t-厚度0.1~1mm Cold rolled or drawn - 1/4 hard (1/4 H) | ≥420 | ≥10 | ||||
| Plates t-厚度0.1~1mm Extra spring hardened (ESH) | ≥5 | |||||
| Plates t-厚度0.1~1mm Spring hardened (SH) | ≥5 | |||||
| Plates t-厚度0.1~1mm Super spring hardened (SSH) | ≥690 | ≥5 | ||||
| Platest-厚度0.1~1mm Annealed (O) | ≥420 | |||||
| Platest-厚度0.1~1mm Extra spring hardened (ESH) | 600–725 | |||||
| Platest-厚度0.1~1mm Spring hardened (SH) | 550–690 | |||||
| Platest-厚度0.1~1mm 超硬化 (EH) | 515–655 | ≥5 |