德国 · DIN

1.0044

DIN 17100 — Hot rolled products in non-alloy steels for general structural applications

化学成分

wt% · 对数刻度
0.0010.010.1110C0.21Mn1.5N0.009P0.045S0.045
  • min – max 范围
  • 典型值

力学性能

按热处理状态分组
屈服强度 Rp0.2≥265 MPa抗拉强度 Rm410–540 MPa伸长率 A≥22 %正火  > 16 <= 40 mm屈服强度 Rp0.2≥255 MPa抗拉强度 Rm410–540 MPa伸长率 A≥21 %正火  > 40 <= 63 mm屈服强度 Rp0.2≥245 MPa抗拉强度 Rm410–540 MPa伸长率 A≥20 %正火  > 63 <= 80 mm屈服强度 Rp0.2≥235 MPa抗拉强度 Rm410–540 MPa伸长率 A≥20 %正火  > 80 <= 100 mm

物理性能

随温度变化
比热容 J/(kg·K)
477 – 500°C

化学成分

元素minmax相似备注
C0.21For thicknesses >= 40 mm C <= 0For thicknesses >= 40 mm C <= 0
Mn1.5
N0.009Depending on P-content N <= 0Depending on P-content N <= 0
P0.045
S0.045

力学性能

热处理 / 状态屈服强度抗拉强度伸长率断面收缩率冲击功硬度
正火  > 16 <= 40 mm≥265 Yield stress is Upper Yield Stress (Reh)410–540≥22 (纵向)
正火  > 40 <= 63 mm≥255 Yield stress is Upper Yield Stress (Reh)410–540≥21 (纵向)
正火  > 63 <= 80 mm≥245 Yield stress is Upper Yield Stress (Reh)410–540≥20 (纵向)
正火  > 80 <= 100 mm≥235 Yield stress is Upper Yield Stress (Reh)410–540≥20 (纵向)
正火  >= 0,5 < 1 mm≤275≤430≤14
正火  >= 1 < 1,5 mm≤275≤430≤15
正火  >= 1,5 < 2 mm≤275≤430≤16
正火  >= 2 < 2,5 mm≤275≤430≤17
正火  >= 2,5 < 3 mm≤275≤430≤18
正火  >= 3 <= 16 mm≥275 Yield stress is Upper Yield Stress (Reh)410–540≥22 (纵向)

物理性能

20.0

弹性模量平均热膨胀系数热导率比热容电阻率密度泊松比
210.00

典型物理值

密度弹性模量泊松比备注
7.86203.000.27–0.30低碳，低合金钢的典型性能数值。此值不来源于标准，它是指示性指标，不能被用于设计用途。

疲劳性能

试验条件
项目内容
ProductSemi Finished products; Thickness: &lt;= 16 mm
ExperimentReversed bending; T: 20°C
Specimen
单调性能
指标数值
屈服强度（MPa）275.0
抗拉强度（MPa）410.0 560.0
伸长率（%）22.0
应力寿命
序号循环次数
11E7

相似牌号

牌号地区标准体系
S275JR意大利UNI
S275JR西班牙UNE
S275JR罗马尼亚STAS
S275JR瑞典SS
S275JR瑞士SNV
S275JR芬兰SFS
S275JR波兰PN
S275JR奥地利ONORM
S275JR匈牙利MSZ
S275JR德国DIN
S275JR捷克CSN
S275JR保加利亚BDS
1.0044意大利UNI
1.0044西班牙UNE
1.0044罗马尼亚STAS
1.0044瑞典SS
1.0044瑞士SNV
1.0044芬兰SFS
1.0044波兰PN
1.0044奥地利ONORM
1.0044挪威NS
1.0044比利时NBN
1.0044匈牙利MSZ
1.0044捷克CSN
1.0044保加利亚BDS
1.0044英国B.S.
1.0044法国AFNOR NF
S275JR挪威NS
S275JR比利时NBN
St4ps俄罗斯GOST
S275JR法国AFNOR NF
S275JR英国B.S.