日本 · JIS
CS75
JIS G4802:1999 — 弹簧用冷轧钢带
化学成分
wt% · 对数刻度- min – max 范围
- 典型值
力学性能
按热处理状态分组化学成分
| Element | min | max | Similar | Remarks |
|---|---|---|---|---|
| C | 0.69 | 0.8 | ||
| Mn | 0.4 | 0.9 | Other values may be specified at the time of ordering provides a range of 0.30% is maintained. | |
| P | 0.035 | may be max.0.020% by agreement | ||
| S | 0.03 | may be max.0.020% by agreement | ||
| Si | 0.1 | 0.35 | Closer silicon ranges can be provided upon agreement at the time of ordering. |
力学性能
| 热处理 / 状态 | 屈服强度 | 抗拉强度 | 伸长率 | 断面收缩率 | 冲击功 | 硬度 |
|---|---|---|---|---|---|---|
| 薄板, 钢带 淬火和回火 t <= 2.5 mm | ≤1321 | |||||
| 薄板, 钢带 退火 | 640 | ≤12 | ||||
| 薄板,HR | 钢带 退火 90；钢带 退火 76；钢带 中间硬化品质 t > 1.0 mm 97；钢带 中间硬化品质 0.36 < t <= 1.0 mm 81；钢带 中间硬化品质 t <= 0.36 mm 89 | |||||
| 薄板,HV | 钢带 中间硬化品质 t > 1.0 mm 240；钢带 中间硬化品质 0.36 < t <= 1.0 mm 250；钢带 中间硬化品质 t <= 0.36 mm 260；钢带 退火 190；钢带 全部硬化品质 t > 1.0 mm ≤240；钢带 全部硬化品质 0.36 < t <= 1.0 mm ≤250；钢带 全部硬化品质 t <= 0.36 mm ≤260；钢带 淬火和回火 t <= 2.5 mm ≤390 |