日本 · JIS
SSW-Q3R Class 2
JIS E5402-1:2005 — 铁路机车车辆 - 实心轮 - 第1部分：质量要求
化学成分
| 元素 | min | max | 相似 | 备注 |
|---|---|---|---|---|
| C | 0.57 | 0.8 | Ladle analysis: 0.60-0.75% | Ladle analysis: 0.60-0.75% |
| Cr | 0.28 | Ladle analysis: max 0.30% | Ladle analysis: max 0.30% | |
| Cu | 0.28 | Ladle analysis: max 0.30% | Ladle analysis: max 0.30% | |
| Mn | 0.46 | 0.94 | Ladle analysis: 0.50-0.90% | Ladle analysis: 0.50-0.90% |
| Mo | 0.08 | for both analysis | for both analysis | |
| Ni | 0.28 | Ladle analysis: max 0.30% | Ladle analysis: max 0.30% | |
| P | 0.055 | Ladle analysis: max 0.045% | Ladle analysis: max 0.045% | |
| S | 0.06 | Ladle analysis: max 0.050% | Ladle analysis: max 0.050% | |
| Si | 0.13 | 0.38 | Ladle analysis: 0.15-0.35% | Ladle analysis: 0.15-0.35% |
| V | 0.05 | for both analysis | for both analysis |
力学性能
| 热处理 / 状态 | 屈服强度 | 抗拉强度 | 伸长率 | 断面收缩率 | 冲击功 | 硬度 |
|---|---|---|---|---|---|---|
| 车轮(锻造或轧制) 轮圈淬火及回火 | ≥770 | 8–12 | HB 311–363 HB(rim) |